Abstract:Porous polystyrene-divinylbenzene (PS-DVB) microspheres of narrow size distribution in the size range of 3.9–4.4 μm were prepared by two-step swelling polymerization methods. Effects of swelling conditions such as swelling activator, temperature, the way of dispersion and dibutyl phthalate (DBP)/seed particle ratio on particle size distribution of the PS-DVB microspheres were investigated in detail. Optimal swelling conditions for the preparation of uniformly sized polystyrene particles have been found as follows: swelling activation agent was dibutyl phthalate (DBP), swelling temperature was 35 °C, dispersion manner was ultrasonic assistant magnetic dispersion, DBP/seed particle ratio was 1–1.5 ml·g-1. It was found that particle size distribution became narrower and swelling time was shortened from more than 24 h to 10 h with the introduction of ultrasonic dispersion, which was attribute to the cavitation effect of ultrasonic and the huge magnetic field action arising therefrom, speeding up the equilibrium of swelling process. Swelling temperature also has significant effect on the monodispersity and particles with the best uniformity could be achieved with the temperature at 35 °C. The possible reason is that process of seed particles absorbing swelling agent through water phase is an equilibrium course of thermodynamics and kinetics.

Preparation of Monodisperse Porous St/DVB Copolymer Microspheres

Preparation of Hollow Microspheres by Dispersion Polymerization-Seeded Swelling Polymerization

Effect of Swelling Process on Monodispersity of Porous Polystyrene-Divinylbenzene Microspheres Prepared by Two-step Swelling Polymerization Methods

Synthesis and Slow-Release Behavior of Functional Porous Microspheres

Swelling Dynamics of Seed-swelling Copolymerization for Preparing Monodisperse Porous Microspheres

Study on the preparation and property of higher hydrophilic poly(styrene-divinylbenzene) porous microsphere

Preparation of Poly (MMA-S-DVB) Microspheres by Suspension Polymerization Method

Preparation of poly(divinylbenzene) microspheres with controllable pore structure using poly(propylene)/toluene as coporogen

Preparation and Superficial Properties of Monodisperse Copolymer Microspheres

Preparation of Large Particle Size Monodispersed Polystyrene Microspheres with High Crosslinked Degree

Preparation of Mondisperse Crosslinked Polystyrene Microspheres with Micron Size

Research on Preparation of Porous Micro-spheres

Preparation of Highly Crosslinked Monodisperse Poly(Styrene-Co-Divinylbenzene)Microspheres by Two-Stage Dispersion Polymerization

Research Progress in Macroporous Styrene-Divinylbenzene Co-Polymer Microspheres

Preparation of Monodisperse Large-Size Cross-Linked P (GMA-St-EGDMA) Microspheres by Two-Step Swelling Polymerization

Preparation of Narrow Size Distribution Crosslinked Polystyrene Microspheres

Preparation and Slow Release Behavior of Porous Hydroquinone-carrying Poly(styrene-divinylbenzene)Microspheres

Preparation of Poly(methyl Methacrylate-Co-styrene) Microspheres by Dispersion Copolymerization

Preparation of porous sulfonated poly(styrene-divinylbenzene) microspheres and its application in hydrophilic and chiral separation

Synthesis of Size-Controlled and Uniform SDB-TPGDA Porous Microspheres by Microfluidic Technology

Preparation of Large Mono-Disperse Polystyrene Micro-Spheres by Dispersion Polymerization