Abstract:A previously proposed method based on soap-free emulsion polymerization with an amphoteric initiator for producing micrometer-sized polystyrene particles was extended to application with methyl methacrylate (MMA). The aggregation and dispersion stability of polymer particles, which have ionizable groups arising from initiator radicals, can be controlled by adjusting the pH of the reaction system accompanied with the addition of ionic monomer. Polymerizations were carried out with 2,2'-azobis[N-(2-carboxyethyl)-2-methylpropionamidine] tetrahydrate amphoteric initiator, NH3/NH4Cl pH buffer, and sodium p-styrenesulfonate anionic monomer (NaSS) in ranges of MMA concentration (0.58-2.32 kmol/M-3 H2O) and NH3 concentration (2.5-20 mol/m(3) H2O) at fixed concentrations of 5 mol/m(3) H2O initiator, 10 mol/m(3) H2O NH4Cl, and 1 mol/m(3) H2O NaSS at 65 degreesC. The addition of NaSS during the polymerization could improve stability in dispersion of particles, which coagulated in the absence of NaSS after the disappearance of monomer drops. An increase in the monomer concentration in the present method could enlarge the particle size without lowering the monodispersity of the particle size distribution. On the other hand, an increase in NH3 concentration decreased the particle size. The highest monodispersity of particle sizes was obtained at a NH3 concentration of 5 mol/m(3) H2O, which gave an average size of 1.5 mum and a coefficient of variation of particle size distribution of 2.2% that was much smaller than the standard criterion for monodispersity, 10%.

Preparation of Micron-sized Monodisperse Poly (Styrene-Co-methyl Methacrylate) Microspheres by Dispersion Copolymerization

Micron-Size Uniform Poly(Methyl Methacrylate) Particles by Dispersion Polymerization in Polar Media 1. Particle Size and Particle Size Distribution

Micron-Size Functional Uniform Pmma Particles by Dispersion Copolymerization in Polar Media

Preparation of Poly(methyl Methacrylate-Co-styrene) Microspheres by Dispersion Copolymerization

Preparation of micron-size crosslinked microspheres by dispersion copolymerization of polystyrene/2,2′-oxy-bisethanol diacrylate

Preparation of Large Mono-Disperse Polystyrene Micro-Spheres by Dispersion Polymerization

Preparation and Superficial Properties of Monodisperse Copolymer Microspheres

Synthesis and Formation Mechanism of Large-Size Monodisperse P(Glycidyl methacrylate-Styrene) Microspheres by Batch Dispersion Copolymerization

Controllable Preparation of Monodisperse Polystyrene Microspheres with Different Sizes by Dispersion Polymerization

Preparation of Surface-Modified Monodisperse Polystyrene Microspheres with Cationic Functional Comonomer

Preparation of Poly (MMA-S-DVB) Microspheres by Suspension Polymerization Method

Preparation of Highly Crosslinked Monodisperse Poly(Styrene-Co-Divinylbenzene)Microspheres by Two-Stage Dispersion Polymerization

Synthesis of Monodisperse Crosslinked St-PEG200DMA Copolymeric Microspheres

Preparation of Microsized Crosslinked Microspheres by Dispersion Copolymerization of Polystyrene/polyethylene Glycol 200-Dimethacrylae

PREPARATION OF MONODISPERSE CROSS-LINKED POLYSTYRENE MICROSPHERES BY COMBINING DISPERSION POLYMERIZATION WITH HYDROTHERMAL PROCESS

Photoinitiated dispersion polymerization of methyl methacrylate: A quick approach to prepare polymer microspheres with narrow size distribution

Study on the Preparation of Monodisperse Polystyrene Microspheres with Narrow Size Distribution

Dispersion Copolymerization of Styrene and Other Vinyl Monomers in Polar Solvents

Dispersion Copolymerization of Styrene and Glycidyl Methacrylate in Polar Solvents

Preparation of micrometer-sized poly(methyl methacrylate) particles with amphoteric initiator in aqueous media.

Synthesis of Monodisperse Crosslinked Polystyrene Microspheres Via Dispersion Copolymerization with the Crosslinker‐postaddition Method