Growth, Thermal and Spectroscopic Characterization of Er3+:NaY(MoO4)2 Crystal

Xiuzhi Li,Zhoubin Lin,Lizhen Zhang,Guofu Wang

DOI: https://doi.org/10.1016/j.jcrysgro.2006.04.100

IF: 1.8

2006-01-01

Journal of Crystal Growth

Abstract:Er3+:NaY(MoO4)2 crystal with dimensions up to Φ21×42mm2 was grown by Czochralski method. Er3+:NaY(MoO4)2 crystal melts congruently at 1125°C. The hardness of Er3+:NaY(MoO4)2 crystal was 314 VDH. The specific heat at 330K is 0.71J/gK (72.9cal/molK). The thermal expansion coefficients are 2.53×10−5 and 1.52×10−5K−1 for c- and a-axes, respectively. The spectroscopic properties of Er3+:NaY(MoO4)2 crystals were investigated. The intensity parameters Ωλ (λ=2,4,6) in Er3+:NaY(MoO4)2 crystal are: Ωλ=17.82×10−20, Ω4=3.277×10−20, Ω6=3.104×10−20 for π-polarization and Ω2=19.74×10−20, Ω4=2.716×10−20, Ω6=1.769×10−20 for σ-polarization. The emission cross sections σem were calculated to be 0.926×10−20cm2 at 1537nm for π-polarization and 1.107×10−20cm2 at 1539nm for σ-polarization.