Growth, Thermal and Laser Properties of Neodymium-doped Sodium Yttrium Double Tungstate Crystal

Zhenxiang Cheng,Shujun Zhang,Kun Fu,Junhai Liu,Huanchu Chen

DOI: https://doi.org/10.1143/JJAP.40.4038

2001-01-01

Abstract:In this paper, the neodymium-doped sodium yttrium double tungstate crystal [Nd:NaY(WO4)(2), designed as Nd:NYW] has been brown by the Czochralski method. The data of thermal expansion and specific heat of the crystal have been measured. The thermal expansion coefficients along X and Z direction are alpha (1) = 3.5 x 10(-6)/K and alpha (2) = 1.77 x 10(-5)/K. respectively. The specific heat is 0.5132 J/g.K. The measured absorption spectra around 800 nm at room temperature show that the crystal has different absorption peaks. 801.25 nm for pi polarization and two peaks 804.04 nm and 812.26 nm for sigma polarization. The peak absorption coefficients are 9.37 cm(-1) (pi) and 3.95 cm(-1) (sigma at 804.04 nm). The fluorescence at room temperature show that the strongest fluorescence is centered at 1060.12 nm. The laser at 1060 nm is demonstrated pumped by a Ti:saphiere laser at 801 nm. The slope efficiency is 38.1%.