Growth, thermal and spectral properties of Nd3+-doped NaGd(MoO4)2 crystal

Xiuzhi Li,Zhoubin Lin,Lizhen Zhang,Guofu Wang

DOI: https://doi.org/10.1016/j.jcrysgro.2006.02.005

IF: 1.8

2006-01-01

Journal of Crystal Growth

Abstract:Nd3+-doped NaGd(MoO4)2 crystal with dimensions Φ21×42mm2 were grown by Czochralski method. Nd3+:NaGd(MoO4)2 crystal melts at 1182°C. The hardness of Nd3+:NaGd(MoO4)2 crystal is 334 VDH. The specific heat is 72.6cal/molK. The thermal expansion coefficients are 2.38×10-5K-1 for c-axis and 1.49×10-5K-1 for a-axis, respectively. The absorption cross-sections of Nd3+:NaGd(MoO4)2 crystal are 15.91×10-20cm2 with a FWHM of 9nm at the 804nm for π-polarization and 3.66×10-20cm2 with a FWHM of 17nm at 807nm for σ-polarization, respectively. The emission cross-section σem are 1.73×10-20cm2 at 1063nm for π-polarization and 1.94×10-20 at 1070nmcm2 for σ-polarization, respectively. The fluorescence lifetime τf is 93.9μs at room temperature.