(1-X)ba4sm9.33ti18o54-xca0.61nd0.26tio3 MICROWAVE DIELECTRIC CERAMICS

LIANG Bingliang,ZHENG Xinghua,NI Weiqing,ZHOU Xiaohong

DOI: https://doi.org/10.3321/j.issn:0454-5648.2006.12.003

2006-01-01

Abstract:Microwave dielectric ceramics of(1–x)Ba4Sm9.33Ti18O54–xCa0.61Nd0.26TiO3[(1–x)BST–xCNT] were prepared by solid statereaction.Effects of composition and sintering temperature on their crystal structure and microwave dielectric properties were investi-gated.A single new tungsten bronze phase was observed in the(1–x)BST–xCNT ceramics when x0.6.A secondary phase appearedand was transformed from Sm2Ti2O7 to a perovskite phase when x≥0.6;and a single perovskite phase was formed eventually.Thedielectric constant e increased steadily with increasing x-value,but the quality factor Qf value increased first,and decreased rapidlyand then increased sharply.Optimal dielectric properties were obtained for the samples sintered at 1 325—1 350 ℃ :e= 75,Qf=8 985GHz,temperature coefficient of resonant frequency τf = –8.2×10–6/ ℃ for x = 0;e=75,Qf =9 552 GHz,τf = –14.4×10–6/ ℃ for x=0.2;e=108.9,Qf=14 919 GHz,τf = 236.2×10–6/ ℃ for x=1.