The Effects of Yttrium Element on Microstructure and Mechanical Properties of Mg–5 Wt.% Zn–2 Wt.% Al Alloy

HH Zou,XQ Zeng,CQ Zhai,WJ Ding

DOI: https://doi.org/10.1016/j.msea.2005.04.011

2005-01-01

Abstract:The addition of yttrium element to the Mg–5wt.% Zn–2wt.% Al alloy leads to the formation of bacillary Al11Y3 phase and polygonal compound Al2Y in the microstructure, and as-cast tensile properties at room temperature are improved substantially when yttrium content is above 1wt.%. Mg–5wt.% Zn–2wt.% Al–2wt.% Y alloy exhibits a combination of high strength and good ductility, the dominant dispersoid in the microstructure is Al11Y3 phase. Large Al2Y phase becomes dominant when yttrium content is above 2.0wt.%, and causes an adverse cutting effect. The study also shows that 2.44wt.% yttrium content in the alloy brings about a mild refining effect.