Study on Shape Memory Effect of Thermosetting Epoxy Resin

WEI Kun,ZHU Guang-ming

DOI: https://doi.org/10.3969/j.issn.1004-2849.2011.02.007

2011-01-01

Abstract:An amorphous epoxy resin(EP) system with lower glass transition temperature was prepared by moderately crosslinking curing reaction after blending between a new polymer curing agent and EP.The some properties(such as mechanical property,shape memory effect,dynamic mechanical property and other properties) of the EP curing system were investigated.The results showed that the EP curing system after moderately crosslinking curing reaction had well shape memory characteristics,and the influences of curing agent content on combination property of the shape memory system were main factor.Its maximal shape recovery rates were all 100%,and the deformation recovery speed was increased with increasing curing agent contents,the maximal deformation recovery speed was 0.023 s-1.The shape fixity ratio was decreased with increasing curing agent contents,and the shape fixity ratio was 100% or 96% when mass fraction of curing agent was 37.5% or 54.5%.