Abstract:Porous Si2N2O/SiC ceramics is facilitated at 1200 °C for 10 min by microwave sintering. Rapid in‐situ production of Si2N2O fibers provided high mechanical properties of the samples. The porosity of the prepared sample is tailorable and the thermal insulation effect is excellent. Two steps strategy were taken to effectively produce porous Si2N2O/SiC ceramics: 1) direct foaming combined with sol‐gel curing at room temperature to form a green body, and 2) sintering assisted by in‐situ production of Si2N2O fibers under microwave sintering conditions. Non‐toxic silica sol was used to provide silicon source for in‐situ synthesis of Si2N2O, the silica sol could form a gel that stabilizes the bubbles, creating a porous structure. A thorough investigation was conducted into how different sintering temperatures affected the microstructure, flexural strength, and porosity of the porous Si2N2O/SiC composites. The main bonding phase in the porous composites was the Si2N2O with fiber morphology. The optimal microwave sintering temperature for fabricating porous Si2N2O/SiC ceramics, using a combination of sol‐gel and direct foaming techniques, has been determined to be 1200 °C. At this temperature, the porosity can be controlled between 73.32% and 83.16% by proportionally adjusting the ratio of the raw materials. Under the condition of high porosity, the thermal radiation is dominant and the thermal conductivity increases with the increase of temperature. With the decrease of porosity, the heat conduction is dominant, and the thermal conductivity decreases with the increase of temperature.

Characterization of Porous Silicon Nitride/silicon Oxynitride Composite Ceramics Produced by Sol Infiltration

Gel casting and properties of porous silicon carbide/silicon nitride composite ceramics

Fabrication And Properties Of Porous Si3n4-Sio2 Ceramics With Dense Surface And Gradient Pore Distribution

Porous Silicon Nitride Ceramics Prepared by Reduction-Nitridation of Silica

Fabrication of low-shrinkage, porous silicon nitride ceramics by addition of a small amount of carbon

Microstructure, Mechanical and Dielectric Properties of Highly Porous Silicon Nitride Ceramics Produced by a New Water-Based Freeze Casting

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

Mechanical and Dielectric Properties of Porous Si3n4-Sio2 Composite Ceramics

Biomorphic Silicon Nitride Ceramics with Fibrous Morphology Prepared by Sol Infiltration and Reduction–Nitridation

3D Printing of Porous Si2N2O Ceramics Based on Strengthened Green Bodies Fabricated Via Strong Colloidal Gel

Fabrication and Mechanical Properties of Porous Silicon Nitride Ceramics from Low-Purity Powder

Preparation of Porous Si2N2O/SiC Ceramics by Microwave Sintering

Porous silicon nitride and SiAlON ceramics: Fabrication and characterization

Biomimetic Synthesis of Porous Si_3N_4 Ceramics

Microstructure and mechanical properties of porous Si 3 N 4 –SiO 2 ceramics fabricated by a process combining carbothermal reduction and sol–gel infiltration–sintering

Preparation And Properties Of High Strength Porous Si3n4 Ceramics

Fabrication and Properties of Porous Si3N4 Ceramic with High Porosity

POROUS Si3N4-SiO2 COMPOSITE CERAMIC AND ITS PROPERTIES

Fabrication and Strengthening of Porous Si3N4 Ceramics by Replacement of Oxide Phase with Si3N4 at Grain Boundary Through Carbothermal Nitridation

Fabrication And Characterization Of In Situ Porous Si3n4-Si2n2o-Bn Ceramic

Electromagnetic wave-transparent porous silicon nitride ceramic prepared by gel-casting combined with in-situ nitridation reaction