Abstract:The long-term stagnation in metal water supply pipes, usually caused by intermittent consumption patterns, will cause significant iron release and water quality deterioration, especially at the terminus of pipelines. Another common phenomenon at the terminus of pipelines is leakage, which is considered helpful by allowing seepage of low-quality drinking water resulting from long-term stagnation. In this study, the effect of laminar flow on alleviating water quality deterioration under different leakage conditions was investigated, and the potential thresholds of the flow rate, which can affect the iron release process, were discussed. Based on a galvanized pipe and ductile cast iron pipe pilot platform, which was established at the terminus of pipelines, this research was carried out by setting a series of leakage rate gradients to analyze the influence of different leakage flow rates on iron release, as well as the relationship with chemical and biological parameters. The results showed that the water quality parameters were obviously influenced by the change in flow velocity. Water quality was gradually improved with an increase in flow velocity, but its change regularity reflected a diversity under different flow rates (p < 0.05). The iron release was remarkably correlated to the redox potential, dissolved oxygen, pH, iron-oxidized bacteria and sulfate-reducing bacteria. The cumulative total iron release (r = 0.587, p < 0.05) and total iron release rate (r = 0.71, p < 0.022) were significantly influenced by the changes in flow velocity. In short, they tended first to increase and then to decrease with an increasing flow velocity with the threshold as approximately 40% of the critical laminar flow velocity (1.16 × 10−3 m/s). For the pipes at the terminus of the drinking water distribution system, when the bulk water was at the critical laminar flow velocity, the concentration of total iron, the quantity and rate of total iron release remain relatively in an ideal and safe situation.

Formational Mechanism and Structural Composition of Aluminum-Containing Scales in Water Supply Pipes

Effects of Chloride and Humic Acid on Iron Release in Water Distribution System

Manganese and iron oxides on pipe surface promote dissolved aluminum accumulation in drinking water distribution systems

Effects of Major Anions on Iron Release in Drinking Water Supply System

Deposition Behavior of Residual Aluminum in Drinking Water Distribution System: Effect of Aluminum Speciation

Formation mechanisms and supervisory prediction of scaling in water supply pipelines: A review

Use of Oxidation-Reduction Potential to Monitor Iron Release from Corroded Iron Pipes in Drinking Water Distribution System

Change regularity of water quality parameters in leakage flow conditions and their relationship with iron release.

Research Progress of Aulminum Disposition and Distribution in Water Supplying System

Factors Affecting the Formation of DBPs by Chlorine Disinfection in Water Distribution System

Controlling iron release of desalinated seawater transmitted in existing grey cast iron pipe

Characteristics of Pipe-Scale in the Pipes of an Urban Drinking Water Distribution System in Eastern China

Metal-release Potential from Iron Corrosion Scales under Stagnant and Active Flow, and Varying Water Quality Conditions.

Study on Electrochemical Reduction Mechanisms of Iron Oxides in Pipe Scale in Drinking Water Distribution System.

Physico-chemical Characteristics of Corrosion Scales from Different Pipes in Drinking Water Distribution Systems

Aluminum Speciation in Drinking Water Distribution System: A Case Study in Northeastern China

The Spatial Distribution of Pollutants in Pipe-Scale of Large-Diameter Pipelines in A Drinking Water Distribution System

Review on corrosion and corrosion scale formation upon unlined cast iron pipes in drinking water distribution systems

Study on the Occurrence of Typical Heavy Metals in Drinking Water and Corrosion Scales in a Large Community in Northern China.

Analysis on Chemical Stability of Metal Ion in Water Distribution System

Identifying effects of pipe material, hydraulic condition, and water composition on elemental accumulation in pipe corrosion scales