Study in the Preparation of Near-spherical Co3O4 Powder

陈培荣,俞志敏

DOI: https://doi.org/10.3969/j.issn.1003-5311.2006.06.025

2006-01-01

Abstract:The Co_3O_4 powder was prepared in thermal decompounding of cobalt carbonate. Using Na_2CO_3 solution as reaction regent, cobalt ions (Co~ 2+ ) precipitate to form cobalt carbonate as precursor. Colloidal precipitation particles are avoided formation because of adding a mount of NH_3 to Na_2CO_3 solution. It is easy to wash and filtrate the precipitation. Therefore the precipitation particles process is high-efficiency and suitable for industrialization. The micrograph of Co_3O_4 powders can be controlled through the molar ratio of Na_2CO_3 to NH_3, pH, the reaction temperature, the addition rate of reagent and the reaction time. Accordingly, near-spherical Co_3O_4 powder with an average diameter of 2.5 μm and the amount of Na less than 0.005% is produced. The near-spherical Co_3O_4 powder has narrow size distribution and excellent dispersing property. ZnO varistors made from the resulting spherical-like Co_3O_4 powder exhibit better electrical properties as compared with those made from the Co_3O_4 powder conventionally prepared by the thermal decomposition of cobalt oxalate.