Abstract:Presently, the main cobalt powder production method is the reduction of cobalt carbonate, and the decomposition process significantly influences the properties of the ensuing cobalt powder. Thus, the objective of this study was to investigate CoCO3 decomposition using thermodynamic simulations and calculations, as well as experiments. The results obtained led to the conclusion that in the absence of oxygen, CoCO3 primarily decomposes into CoO and CO2. However, in the presence of oxygen, it preferentially undergoes oxidation decomposition, generating Co3O4 and CO2, while the unreacted CoCO3 subsequently decomposed forming more CoO when O2 was exhausted. Additionally, Co3O4 decomposed to CoO and O2 at high temperatures. TG-DSC-MS analyses showed that the temperature at which CoCO3 decomposed into CoO was 332 °C. The analysis of the CoCO3 decomposition process performed in an inert atmosphere showed that the decomposition product, CoO was generated at temperatures above 300 °C. Furthermore, SEM results showed that the morphology of the CoO obtained depends on that of the raw material (CoCO3), and a higher temperature induced agglomeration; thus, increasing CoO size. Lower decomposition temperatures, higher gas flow rates, and lower heating rates resulted in a decrease in CoO particle size.

Preparation and characterization of Co_3O_4 by thermal decomposition from Co_2(OH)_2CO_3

Synthesis And Characterization Of Mocvd Precursor Fe(Dpm)(3)

Synthesis and Their Physicochemical Behaviors of Flower-Like Co3O4 Microspheres

Preparation of Nanosized GdCoO 3 Powder Using Amorphous Heteronuclear Complex As a Precursor

Structure and Catalytic Activity of 3D Macro/mesoporous Co3O4 for CO Oxidation Prepared by a Facile Self-Sustained Decomposition of Metal–organic Complexes

Study on thermodynamic equilibrium and character inheritance of cobalt carbonate decomposition

Studies on the nanocrystalline Co3O4 by wet synthesis and its microstructure

Study of preparation of cobalt cerium complex oxides catalyst by sol-gel method

The Synthesis and Characteristic of Co3O4 Nanocrystals

Synthesis and Characterization of Ca3Co4O9 Nanoparticles by Citrate Sol-Gel Method

Study on the preparation and the properties of cobalt cerium mixed oxides catalysts with ultrafine particals

Synthesis And Characterization Of Ca2co2o5 Powders By Coprecipitation Method

Effect of cobalt precursors on the dispersion, reduction, and CO oxidation of CoOx/γ-Al2O3 catalysts calcined in N2

Studies on the Preparation of Co3O4/CeO2 Materials and Their Applications on CO Oxidation at Low-Temperature

Moderate temperature synthesis of nanocrystalline Co3O4 via gel hydrothermal oxidation

Preparation of MoO 3 powder by hydrothermal method

Controllable Synthesis of Co3O4 Octahedra with the Assistance of C2 O2-4

Preparation and Characterization of Cesium and Cobalt Complex Oxide

Co3O4 nanoparticles/Bi2O3 nanosheets: One step synthesis, high-efficiency thermal catalytic performance, and catalytic mechanism research

Cobalt hydroxide nanosheets and their thermal decomposition to cobalt oxide nanorings.

Thermal decomposition analysis of Co2+ content alginic acid cross-linked structure for the synthesis of cobalt oxides