Abstract:A modified nano-calcium carbonate (R-CCR) was prepared by coating a layer of unsaturated hydroxylfatty acid on the surface of CCR powders using a solid state method; the latter were commercial nano-CaCO 3 modified with stearic acid. FTIR studies indicate that the modifier is combined on the surface of CaCO 3 . PP/EPDM/nano-CaCO 3 ternary composites were prepared by a melt-mixing method. SEM and TEM were utilized to examine the morphology of the composites. The tensile fractured surface of PP/EPDM/R-CCR showed a fibroid morphology and large-scale yield deformation. The impact fractured surface showed that the amount of cavities in the PP/EPDM/R-CCR system was increased, however their size diminished obviously. R-CCR particles were dispersed uniformly in the PP matrix, and their compatibility was distinctly improved as compared to CCR when the amount of R-CCR was 15 h −1 . The tensile strength remained nearly constant (reduced from 27.6 MPa to 27.5 MPa), while the impact strength increased from 9.6 kJ/m 2 to 15.4 kJ/m 2 as CCR was replaced by R-CCR. Meanwhile, the bending strength and bending modulus also increased correspondingly. Furthermore, the impact strength of PP/EPDM/R-CCR was maintained at a high level (15.4 kJ/m 2 ), which was more than the sum of that of PP/EPDM and PP/R-CCR (6.6 kJ/m 2 and 6.1 kJ/m 2 respectively). This indicates that the R-CCR and EPDM have a significant synergistic toughening effect on PP while maintaining the strength and modulus of virgin PP. Both the storage modulus G′ and loss modulus G″ of PP/EPDM and PP/EPDM/R-CCR composites increase with increasing frequency, but the values of G′ and G″ of the tertiary composite are relatively higher than those of the binary system. The loss factor and viscosity decrease with increasing frequency, but there is little difference between tertiary and binary composites. The apparent viscosity η of the tertiary system containing R-CCR is lower than that of the tertiary system containing CCR and virgin PP. The viscosity of the composites sig-nificantly decreases with increasing shear rate. The mea-sured mechanical properties of the composites indicate that replacing CCR with R-CCR for binary composites could simultaneously enhance the toughness and strength of PP.

Effect of Screw Configuration on Online Rheological Property of Polypropylene/Nano-Calcium Carbonate Composite

Evolution of residence time distribution and fill degree in co-rotating twin-screw extruder

Effect of Screw Configuration and Screw Speed on the Mechanical and Rheology Properties of Glass Fiber Reinforced Polyamide 66

Study on the Properties and Structure of Polypropylene Modified with Nano-Sized CaCO_3

Effect of high‐shear mixing by twin‐screw extruder on the dispersion and homogeneity of polyacrylonitrile/carbon nanotube composite solution

Effect of Oleic Acid-modified Nano-CaCO3 on the Crystallization Behavior and Mechanical Properties of Polypropylene

Continuous film casting of polycarbonate/single‐walled carbon nanotubes composites with ultrasound‐assisted twin‐screw extruder: Effect of screw configuration

Rheological Properties of Neat and Calcium Carbonate Particles Filled Polypropylene Blends under Axial Vibration Force Field

Rheological and extrusion behavior of intercalated high-impact polystyrene/organomontmorillonite nanocomposites

Enhancing a Multi-Field-synergy Process for Polymer Composite Plasticization: A Novel Design Concept for Screw to Facilitate Phase-to-phase Thermal and Molecular Mobility

Effects of processing on mechanical properties of polypropylene composites

Ultrasonic Twin Screw Compounding of Polypropylene with Carbon Nanotubes, Graphene Nanoplates and Carbon Black

Crystallization Behaviour and Mechanical Properties of Polypropylene Copolymer/Silicon Dioxide Nanocomposites

Investigation Into Poly(propylene)/Montmorillonite/Calcium Carbonate Nanocomposites

Effects of Nanoparticle Treatment on the Crystallization Behavior and Mechanical Properties of Polypropylene/calcium Carbonate Nanocomposites

Effect of different compatibilization routes on the mechanical, thermal and rheological properties of polypropylene/cellulose nanocrystals nanocomposites

Experiment and Simulation of Foaming Injection Molding of Polypropylene/nano-Calcium Carbonate Composites by Supercritical Carbon Dioxide

Study on the Preparation and Properties of Caco3/Polypropylene Composite Materials

Electrical Resistivity, Crystallization and Mechanical Properties of Polypropylene/Multi-Walled Carbon Nanotube/Calcium Carbonate Composites Prepared by Melt Mixing

Effect of Unsaturated Hydroxyl-Fatty Acid Modified Nano-Caco3 on the Morphological and Rheological Behavior of PP

Effect of Wet Surface Treated Nano-Sio2 on Mechanical Properties of Polypropylene Composite