Microscopic Hardness and Dynamic Mechanical Analysis of Rapidly Solidified Fe-based Amorphous Alloys
P. C. Zhang,Y. J. Hu,J. Chang,H. P. Wang
DOI: https://doi.org/10.1016/j.jallcom.2020.157957
IF: 6.2
2021-01-01
Journal of Alloys and Compounds
Abstract:A systematic work was conducted to investigate the nanoindentation, dynamic relaxation, high-temperature rheological behavior, and structural relaxation after high-temperature deformation of Fe52-xCo20NixB19Si5Nb4 (x = 7,12,17, labeled as S-1, S-2 and S-3) metallic glass. The results of nanoindentation indicate that the hardness of amorphous alloy reduces first and then enhances with the increase of Ni content. S-1 alloy exhibits the highest hardness of 13-16 GPa, while relatively excellent compression plasticity is reached in S-2 alloy. Besides, the glass transition temperature (T-g), initial crystallization temperature (T-x), alpha relaxation temperature (T-alpha) and internal friction change at different temperatures were determined and compared. The critical temperature, strain rate during non-Newton to Newtonian rheology and Newtonian viscosity at T-g temperature were discussed. Moreover, it was found that the activation volume improved and then decreased due to structural relaxation. At last, combined with the width of the supercooled liquid region, relaxation behavior and rheological viscosity at high temperature, the microstructure evolution of the three kinds of metallic glass under T-g temperature deformation was explained. (C) 2020 Elsevier B.V. All rights reserved.