Abstract:Room-temperature nanoindentation creep behavior of bulk metallic glasses (BMGs) with various glass transition temperature (Tg) was investigated through using spherical indenter. The activation information of shear transformation zone (STZs) was studied by analyzing statistical distributions of the first pop-in events during nanoindentation. It was revealed that the higher Tg the BMG possessed, the more difficult the creep deformation became, being linked with lower ε̇s/Pmax (apparent steady creep strain rate normalized by applied maximum load), which was discovered to be a good indicator of room-temperature nanoindentation creep resistance. We demonstrated that it was the smaller nucleation site density, m, and higher activation energy upon yielding, WSTZ, that hindered the activation and cooperative shearing of STZs, causing better creep resistance in harder BMGs with higher Tg. However, no dependence of creep resistance on structural heterogeneity in each BMG was observed. Intrinsically, in local harder region as compared to local softer region, the lower WSTZ promotes activation of STZs and reduce creep resistance, while the smaller m denotes less potential nucleation site prone to be activated and helps to enhance creep resistance. It is this kind of competition that gives rise to the independence of creep resistance on structural heterogeneity in each BMG.

Room-temperature nanoindentation measurements of La-based bulk metallic glass

Atomic-scale Heterogeneity in Large-Plasticity Cu-doped Metallic Glasses

Instrumented indentation study of plastic deformation in bulk metallic glasses

Plastic deformation behavior of Fe40Ni40P14B6 bulk metallic glass investigated by nanoindentation

Nanoindentation study on room-temperature creep behavior of Ir33Ni28Ta39 bulk metallic glass

Tension and stress relaxation behavior of a La-based bulk metallic glass

Structural transformation and rheological processes in bulk metallic glass Zr41Ti14Cu12.5Ni10Be22.5

Glass Formability, Thermal Stability and Mechanical Properties of La-Based Bulk Metallic Glasses

Dependence of Room-Temperature Nanoindentation Creep Behavior and Shear Transformation Zone on the Glass Transition Temperature in Bulk Metallic Glasses

Mechanical Properties of Monolithic Zr62Al8Ni13Cu17 Bulk Metallic Glass

Thermal expansion of La-based BMG studied by in situ high-energy X-ray diffraction

Local Strain Behavior of Bulk Metallic Glasses under Tension Studied by in Situ X-Ray Diffraction

Nanoindentation Study on the Room Temperature Creep Characteristics of A Senary Ti16.7zr16.7hf16.7cu16.7ni16.7be16.7 High Entropy Bulk Metallic Glass

La-based bulk metallic glass failure analysis under static and dynamic loading

Structures at Glassy, Supercooled Liquid, and Liquid States in La-Based Bulk Metallic Glasses

La-based bulk metallic glasses with critical diameter up to 30mm

Direct in situ observation of metallic glass deformation by real-time nano-scale indentation

Thermal Expansion Of A La-Based Bulk Metallic Glass: Insight From In Situ High-Energy X-Ray Diffraction

Tensile deformation of metallic glass and shape memory alloy nanolaminates

Non-localized deformation in metallic alloys with amorphous structure

Study of mechanical deformation in bulk metallic glass through instrumented indentation