Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Synthesis of Sb2O3 nanorods under hydrothermal conditions

Growth of Crystalline Sb2S3 Nanorods by Hydrothermal Method

Low Temperature Growth of Bismuth Sulfide Nanorods by a Hydrothermal Method

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

A new hydrothermal route for synthesis of molybdenum disulphide nanorods and related nanostructures

Synthesis and Photoelectrocatalytic Performance of Sb2S3 Nanorods from Natural Stibnite

A Single-Source Approach to Bi2s3 and Sb2s3 Nanorods Via A Hydrothermal Treatment

Hydrothermal preparation of α-MnS nanorods from elements

Hydrothermal Synthesis of Flower-Like Bi2S3with Nanorods in the Diameter Region of 30 Nm

Synthesis of Novel Sbsi Nanorods by A Hydrothermal Method

Single crystalline CdS nanorods fabricated by a novel hydrothermal method

Synthesis of One-Dimensional Chalcogenides by a Novel Hydrothermal Process

Synthesis and characterization of Sb2Se3 nanorods

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Synthesis of Novel Sb2O3 and Sb2O5 Nanorods

Preparation And Characterization Of Bismuth Sulfide Single Crystal Nanorods In Ionic Liquids

A Novel Hydrothermal Synthesis of Single Crystalline Pbs Nanorods and Their Characterization

H2SO4-assisted hydrothermal preparation of γ-AlOOH nanorods

A Novel and Low-Temperature Hydrothermal Synthesis of SnO 2 Nanorods

Scalable Synthesis of Sb(III)Sb(V)O4 Nanorods from Sb2O5 Powder Via Solvothermal Processing

Large-Scale Synthesis of Bismuth Sulfide Nanorods by Microwave Irradiation