Abstract:A water-based route has been demonstrated for synthesizing ZnSe and Cd-doped ZnSe (ZnSe(ZnxCd1-xSe, 0 < x < 1) quantum dots (QDs) that have tunable and narrow photo luminescence (PL) peaks from the ultraviolet A (UVA) to the blue range (350-490 nm) with full-width at half-maximum (fwhm) values of 24-36 nm. Hydrazine (N2H4) was used to maintain oxygen-free conditions, allowing the reaction vessel to be open to air. The properties of the QDs were controlled using the thiol ligands, 3-mercaptopropionic acid (MPA), thiolglycolic acid (TGA), and L-glutathione (GSH). On the basis of optical spectra, linear three-carbon MPA attenuated nucleation and growth, yielding small ZnSe QDs with a high density of surface defects. In contrast, TGA and GSH produced larger ZnSe QDs with lower surface defect densities. The absorption spectra show that growth was more uniform and better controlled with linear two-carbon TGA than branched bifunctional GSH. After 20 min of growth TGA-capped ZnSe had an average diameter of 2.5 nm based on high-resolution transmission electron microscopy images; these nanocrystals had an absorbance peak maximum of approximately 340 nm (3.65 eV) and a band gap PL emission peak at 372 nm (3.34 eV). Highly fluorescent ZnxCd1-xSe QDs were fabricated by adding a Cd-thiol complex directly to ZnSe QD solutions; PL peaks were tuned in the blue range (400-490 nm) by changing the Zn to Cd ratio. The Cd-bearing nanocrystals contained proportionally more Se based on X-ray photoelectron spectroscopy, and Cd-Se bonds had ionic character, in contrast to primarily covalent Zn-Se bonds.

Preparation of Group IIB Selenide Nanoparticles Using Soft-Hard Dual Template Method

Control synthesis of semiconductor ZnSe quasi-nanospheres by reverse micelles soft template

Preparation of Hollow CdSe Nanospheres

Facile synthesis of CuSe nanoparticles and high-quality single-crystal two-dimensional hexagonal nanoplatelets with tunable near-infrared optical absorption

Sonochemical Method for the Preparation of Monodisperse Spherical and Rectangular Lead Selenide Nanoparticles

General Sonochemical Method for the Preparation of Nanophasic Selenides: Synthesis of ZnSe Nanoparticles

An Aqueous Approach to ZnSe and CdSe Semiconductor Nanocrystals

Synthesis of Hgse Quantum Dots Through Templates Controlling and Gas-Liquid Transport with Emulsion Liquid Membrane System

Wet Synthesis and Characterization of Mse (M = Cd, Hg) Nanocrystallites at Room Temperature

Size- and Shape-Controlled Synthesis of ZnSe Nanocrystals Using SeO2 As Selenium Precursor.

Cu2−xSe nanooctahedra: controllable synthesis and optoelectronic properties

Preparation and optical properties of silica gel–glass doped with ZnSe nanoparticles

One-Pot Hydrothermal Synthesis Of Znse Hollow Nanospheres From An Ionic Liquid Precursor

Sonochemical Synthesis of Silver, Copper and Lead Selenides

A Complex‐Based Soft Template Route to PbSe Nanowires

Preparation of ZnSe Quantum Dots Embedded in SiO2 Thin Films by Sol–gel Process

Solvothermal synthesis and characterization of CdSe nanocrystals with controllable phase and morphology

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

Preparation of Hydrophobic Quantum Dots Using Oleylamine-Hydrogen Selenide Complex As Precursor

Synthesis Of Cdse, Znse, And Znxcd1-Xse Nanocrystals And Their Silica Sheathed Core/Shell Structures

Photochemical preparation of rectangular PbSe and CdSe nanoparticles