Abstract:High quality zinc blende ZnSe and ZnSe/ZnS core/shell nanocrystals have been synthesized by two converse injection methods (i.e. zinc precursor injection or selenium precursor injection) when Se-ODE complex was chosen as the phosphine-free selenium precursor. Absorption spectroscopy, fluorescence spectroscopy, X-ray diffraction (XRD), and transmission electron microscopy (TEM) were used to characterize the as-synthesized ZnSe and ZnSe/ZnS nanocrystals. The quality of the as-prepared ZnSe nanocrystals reached the same high level compared with the method using phosphine selenium precursors since the quantum yields were between 40 and 60% and photoluminescence (PL) full width at half-maximum (FWHM) was well controlled between 14 and 17 nm. The parameter window for the growth of high quality ZnSe nanocrystals was found to be much broader and monodisperse ZnSe nanocrystals were synthesized successfully even when the reaction temperature was set as low as 240 degrees C. As cores, such zinc blende ZnSe nanocrystals were also used to synthesize ZnSe/ZnS core/shell nanocrystals with high fluorescence quantum yields of 70%. Cu(2+) or Mn(2+) doped ZnSe nanocrystals were also synthesized by simply modifying this phosphine-free method. The emission range has been extended to 500 and 600 nm with the use of Cu(2+) and Mn(2+) dopants compared with the emission coverage of ZnSe at around 400 nm. This is the first totally "green approach" (i.e. phosphine-free synthesis) for the synthesis of high quality ZnSe, ZnSe/ZnS, and Cu(2+) or Mn(2+) doped ZnSe nanocrystals.

General Sonochemical Method for the Preparation of Nanophasic Selenides: Synthesis of ZnSe Nanoparticles

Sonochemical Method for the Preparation of Monodisperse Spherical and Rectangular Lead Selenide Nanoparticles

A Novel Sonochemical Method for the Preparation of Nanophasic Sulfides: Synthesis of HgS and PbS Nanoparticles

A Novel Method for the Preparation of Lead Selenide: Pulse Sonoelectrochemical Synthesis of Lead Selenide Nanoparticles

Sonochemical Synthesis of Copper Selenides Nanocrystals with Different Phases

Size- and Shape-Controlled Synthesis of ZnSe Nanocrystals Using SeO2 As Selenium Precursor.

Phosphine-free Synthesis of High Quality ZnSe, ZnSe/ZnS, and Cu-, Mn-doped ZnSe Nanocrystals.

An Aqueous Approach to ZnSe and CdSe Semiconductor Nanocrystals

Sonochemical synthesis of size-controlled mercury selenide nanoparticles

Studies of synthesis and optical properties of ZnS nanocrystals

Sonochemical Synthesis of Silver, Copper and Lead Selenides

Microwave-Assisted Aqueous Synthesis: A Rapid Approach to Prepare Highly Luminescent Znse(S) Alloyed Quantum Dots

Preparation of ZnSe Quantum Dots Embedded in SiO2 Thin Films by Sol–gel Process

The synthesis and photocatalytic activity of ZnSe microspheres.

Hydrothermal Preparation and Optical Absorption of ZnSe Nanocrystals

Sonochemical Synthesis and Mechanistic Study of Copper Selenides Cu2-Xse, Beta-Cuse, and Cu3se2

Application and preparation of ZnSe nanometer powder by reduction process

Nanoparticle Based Preparation Method of Cu_2ZnSn(SSe)_4 Thin Films

Preparation of Zns Nanoparticles by Ultrasonic Radiation Method

A Solvothermal Route to Wurtzite ZnSe Nanoparticles

Photochemical Synthesis of Bi2Se3 Nanosphere and Nanorods