Abstract:<p>To provide the process parameters for preparing semi-solid billets, the impacts of heating temperature on recrystallization of a hot-extruded 6A02 aluminum alloy in solid and semi-solid temperature ranges were studied. The static recrystallization (SRX) even occurred at semi-solid temperature due to the low deformation ratio in the starting hot-extruded sample. Almost all elongated grains were transformed into equiaxed grains at immediate 630 °C. But not all grains with equiaxed shape were pure recrystallized grains, and small static recrystallized grain even emerged inside them. Bulk insoluble second particles including Fe, Mn, and Si were distributed at the grain boundaries. With the increasing of heating temperature, Vickers hardness increased firstly, then decreased and increased finally. And it was relevant with external force direction. According to the electron backscatter diffraction (EBSD) analysis, the fraction of the recrystallized, sub-structured and deformed grains changed little at 540 °C, but varied greatly at 600 °C and 630 °C. The contents of<111> and<100> fiber deformed textures as well as {100}<001> Cube texture showed analogical variation tendencies. The dislocation densities decreased roughly with temperature both from grain-based and kernel-based perspectives. Inhomogeneous deformation existed in an individual grain. Schmid factor had great relevance with external force direction and the gaps were narrowed by the equiaxed microstructure. In the isothermal deformation test, the liquid film was thickened and voids emerged in the shear-deformation region.</p>

Reheating Process for the Semi-solid A356 Alloy

Numerical Simulation of Cavity-Filling Procedures for Micro-Pin-fin Array Thixoforming with Semi-Solid A356 Aluminium Alloy

Study on Billet Temperature Prediction and Furnace Temperature Optimal Setting of Regenerative Reheating Furnace

Rheologic Properties of Aluminum Alloy A356 Bille ts Produced by Semisolid Continuous Casting Process

Effect of Heating Process on Semi-solid Microstructure of Cold Rolled 6061 Aluminum Alloy

High-temperature Oxidation Behavior of AlCoCrCuFeNi High-Entropy Alloy by Selective Laser Melting

Preparation of Semi-Solid A356 Al Alloy Slurry by Repeated Heating-Cooling Method with Elliptical-Twisted Tubes

Microstructure evolution of hot pressed AZ91D alloy chips reheated to semi-solid state

Effects of Heating Temperatures on Microstructure of Semi-solid AZ91D Magnesium Alloy During Partial Remelting

Effect of Annealing Process on Microstructure and Properties of Rolled Semi-solid Billet

Recrystallization process of hot-extruded 6A02 aluminum alloy in solid and semi-solid temperature ranges

Thermomechanical processing of AA6061 billets for semi-solid forming

Recrystallization of Hot-Rolled 2A14 Alloy during Semisolid Temperature Annealing Process

Semi-solid processing of the primary aluminium die casting alloy A365

On-line Preparation Technology of Semi-Solid Slurry of A356.2 Alloy

Microstructure Evolution of Semi-Solid 2024 Alloy During Two-Step Reheating Process

Fatigue property of semisolid A357 aluminum alloy under different heat treatment conditions

Effects of temperature and time on three-dimensional microstructural evolution of semi-solid 2A14 aluminum alloy during short process preparation of semi-solid billets

Effect of New Flux on the Purification of A356 Aluminum Alloy

Influences of Master Alloys and Their Preparation Conditions on Microstructures of Semi-solid A356 Alloy Slurries

Effects of Isothermal Temperature and Soaking Time on Water Quenched Microstructure of Nickel-Based Superalloy GH3536 Semi-Solid Billets