Abstract:A nearly pure 2223 phase of the ceramic superconductor Bi1.8Pb0.3Sb0.1Sr2Ca2Cu3O10−δ was obtained by solid-state reaction in air. The samples showed a semiconducting behavior when the temperature was higher than 140 K. The electrical resistance began to drop at 140 K and went to zero at 92 K. Their a.c. magnetic susceptibility showed two transitions at 130 and 89 K, but the 110 K transition was absent. These transitions were stable during cycling for three times from 77 K to room temperature. X-ray diffraction revealed that there was no 2212 or 2201 phase in these samples but only a small amount of monoclinic phase before and after cycling from 77 K to room temperature. SEM images showed that the grains of the monoclinic phase segregated on the surface of the sample and at the grain boundaries inside the sample, which is the reason for the sample's poor superconductivity and the decrease in zero resistance. Evidence from TEM and SEM equipped with a wavelength dispersive meter indicated distortion of the 2223 phase. These distorted 2223 crystals may be responsible for the 130 K superconductivity.

111 K Superconductor Bi1.7Pb0.45Sr2Ca2Cu3Oy Prepared by Means of the Three-Step Reaction Process

112–114 K superconductors Bi1.8Pb0.3Sr2Ca2Cu3Oy by means of a three-step reaction process

BiPbSrCaCuO Superconductor Prepared by a Three-Step Reaction Process

PREPARATION AND SUPERCONDUCTIVITY OF SINGLE PHASE Bi1.65Pb0.35Sr2Ca2Cu3Oy WITH ZERO RESISTANCE TEMPERATURE 106.5K

Preparation And Phase Research Of The 110-K High-Tc Superconductor Bi2sr2ca2cu3oy Doped With Sb And Pb

Preparation and Superconductivity of the High-Tc Phase of Pb-doped Bi-Sr-Ca-Cu-O Superconductor

Preparation of 110k Superconductor in Bi-Sr-Ca-Cu-O System

Study On Bi(Pb, Sb)Srcacuo Superconductors Prepared By The Oxalate Coprecipitation Technique

PHASE TRANSFORMATION AND SUPERCONDUCTIVITY OF 110K SUPERCONDUCTOR IN (bi, Pb)-Sr-Ca-Cu-O SYSTEM

Superconducting Properties In Bi2-X-Ypbxsbysr2ca2co3oz (X=0,0.1, 0.3, 0.5 Y=0, 0.1)

The 130 K High- T c superconductor in the system Bi-Sr-Ca-Cu-O doped with Sb and Pb

Effect of Bi/Pb Ratio and Annealing Temperature on T C and Formation of High- T C Phase in Bi-Pb-Sr-Ca-Cu-O Superconductor

Superconductivity at 77K in (pb, Cu)Sr2(Ca, Y)Cu2O7 by Post-Annealing

ZERO RESISTANCE AT 113 K IN THE (Bi1.9−xPbxSb0.1)Sr2Ca2Cu3Oy SYSTEM (x=0.1, 0.2, 0.3, 0.4)

Preparation and Superconductivity of Bi3PbCa3Sr3Cu4Oy

The reaction process of the Bi-Sr-Ca-Cu-O system and the forming mechanism of the 2212 superconducting phase

Preparative And Structural Studies On The Superconducting Phase (Bi1.7pb0.2in0.1)Sr2ca2cu3o10

Influence of Heat Treatment on the Superconducting Properties of Bi1.6Pb0.3Sb0.1Sr2Ca2Cu3O Y

Peculiar Property of Single Phase Bi 3 PbCa 3 Sr 3 Cu 4 O Y

Synthesis, Structure, and Properties of the Superconductor Ba 1− x K z Bi 1− y Pb y O 3

Superconducting Oxide Dy-Ba-Cu-O with TC(π=0) Beyond 90K