Abstract:SiC nanowires have been synthesized by microwave-vacuum heating method at 1480°C, using silicon powders, silica dioxide powders and artificial graphite as raw materials. SEM, TEM and XRD were employed to investigate the micro-structure of obtained specimens. It was shown that β-SiC can be directly synthesized directly without any catalyst on the basis of the vapor-solid (VS) growth mechanism. The obtained specimens exhibited various morphologies and sizes, due to the differences in the reaction temperatures and the distribution of components in the crucible. Products existed in upper crucible were bright-green and more pure, mainly consisting of nanorods with a diameter of about 150nm and some SiC micro-crystals. At the same time, the surface oxidation phenomenon was not obvious. As to the grey-green products existed in other zone, lots of SiC/SiO2 coaxial nanowires with a diameter around 20-50 nm (the thickness of SiO2 surface layer was about 2nm) were successfully obtained. Besides, there also remained some un-reacted graphite and silica dioxide. The excitation light with wavelength of 240nm was used to test the photoluminescence properties of the products. Results showed that both of the SiC nanorods and SiC/SiO2 coaxial nanowires exhibited a strong broad photoluminescence peak at wavelength of about 390nm, displaying a higher degree of blue-shift in comparison to the reported luminescence results of β-SiC nanomaterials.

Silicon carbide hollow nanospheres, nanowires and coaxial nanowires

3C-Sic Nanowires and Micro-Scaled Polyhedra: Synthesis, Characterization and Properties

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Synthesis and Characteristics of Cubic Silicon Carbide Nanospheres with Smooth Surfaces.

Vapor-Solid Reaction for Silicon Carbide Hollow Spherical Nanocrystals

Large-scale synthesis and characterization of hexagonal prism-shaped SiC nanowires.

Crystalline Silicon Carbide Nanoparticles Encapsulated in Branched Wavelike Carbon Nanotubes: Synthesis and Optical Properties

Syntheses and Growth Mechanisms of 3C-Sic Nanostructures from Carbon and Silicon Powders.

Silicon Carbide Nanowires Synthesized with Phenolic Resin and Silicon Powders

Synthesis and Characterization of SiC Nanowires Through a Reduction−Carburization Route

Synthesis and Raman Scattering of Β-Sic/sio2 Core–shell Nanowires

Synthesis of Silicon Carbide Nanowires in a Catalyst-Assisted Process

Synthesis, Characterization, and Photoluminescence Properties of Bulk-Quantity Β-Sic/siox Coaxial Nanowires

Study on the Preparation and Micro-Structural Characterization of SiC Nanowires Obtained by Direct Microwave Heating

Large-scale Synthesis and Photoluminescence Properties of Hexagonal-Shaped SiC Nanowires

Selective Synthesis Of 3c-Sic Hollow Nanospheres And Nanowires

Tuning the morphologies of SiC nanowires via the control of growth temperature, and their photoluminescence properties.

Growth Of Sic Nanorods At Low Temperature

Thermal evaporation and solution strategies to novel nanoarchitectures of silicon carbide

Low temperature synthesis and photoluminescence of cubic silicon carbide

Synthesis and Characterization of SiC Nanowires Using Silicon Evaporation