Abstract:A method for preparing CdS nanoparticles within the porous confines of a mesoporous starch gel is described. This method utilises the combined colloidal and flexible chemical nature of a porous polysaccharide (i.e. starch) gel to limit CdS growth. The resulting hybrid gels can be dried to produce CdS/starch materials with high surface areas, predominantly mesoporous characteristics and scope for high CdS loading. The synthesis is conducted in aqueous alcoholic solutions without the need for expensive preparation techniques or additional protection/templating strategies. Materials were prepared at increasing CdS loadings on the starch gel, which confined nanoparticle growth and directed size/surface coverage, dispersion and UV-vis absorption profile. The resulting powders presented large mesopore domains with high volumes (pore diameters > 10 nm; V-meso > 0.5 cm(3) g(-1)) and surface areas (S-BET > 170 m(2) g(-1)), interestingly effectively increasing with CdS loading. The synthesised CdS nanoparticles were characterised in the 5-40 nm range of a cubic crystalline structure, increasing in size with loading. A complete surface coverage of the starch gel structure occurs at a CdS/starch ratio = 1 (w/w), allowing the synthesis of a unique mesoporous CdS/polysaccharide hybrid. The presented route is simple, green and in principle extendable to a wide range of QDs and polysaccharide gels, whereby the porous polysaccharide gel acts as the deposition point of Cd2+, directing and stabilising both the growth of the inorganic CdS phase and the expanded high surface area polysaccharide form. (C) 2014 The Authors. Published by Elsevier B.V. All rights reserved.

“Green” Synthesis of Starch Capped CdSe Nanoparticles at Room Temperature

Synthesis of Highly Luminescent Mercaptosuccinic Acid-Coated Cdse Nanocrystals under Atmospheric Conditions

Preparation and Characterization of Polyvinyl Alcohol-Capped CdSe Nanoparticles at Room Temperature

Water-Soluble Cdse and Cdse/Cds Nanocrystals: A Greener Synthetic Route

Synthesis of monodispersed CdSe nanocrystals in poly(styrene-alt-maleic anhydride) at room temperature

Single Step Synthesis of CdSeS Nanorods with Chemical Composition Gradients

Facile Phosphine-Free Synthesis of CdSe/ZnS Core/Shell Nanocrystals Without Precursor Injection

Size-, Shape-, and Assembly-Controlled Synthesis of Cu2−xSe Nanocrystalsvia a Non-Injection Phosphine-Free Colloidal Method

Preparation of CdSe Quantum Dots with Full Color Emission Based on a Room Temperature Injection Technique.

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

Dielectric and optical studies of CdSe nanoparticles: green synthesis

Synthesis of Green CdSe/chitosan Quantum Dots Using a Polymer-Assisted Γ-Radiation Route

Synthesis of Cdse nanocrystals in aqueous solution

Colloidal Construction of Porous Polysaccharide-Supported Cadmium Sulphide

Room Temperature Synthesis of Cubic Nanocrystalline CdSe in Aqueous Solution

Synthesis of Efficiently Green Luminescent CdSe/ZnS Nanocrystals Via Microfluidic Reaction

A surfactant-free recipe for shape-controlled synthesis of CdSe nanocrystals.

"Green" Synthesis of Size Controllable Prussian Blue Nanoparticles Stabilized by Soluble Starch.

Investigations on structural and optical properties of starch capped ZnS nanoparticles synthesized by microwave irradiation method

Ultrasound assisted synthesis of starch-capped Cu2O NPs towards the degradation of dye and its anti-lung carcinoma properties

Synthesis and Characterization of Cdse Nanocrystals Capped by Cds