Effect of Al-3 wt% Al2O3 master alloy fabricated by calcined kaolin on grain refinement and mechanical properties of A356 alloy
Jiasheng Xu,Gang Chen,Zhenya Zhang,Yutao Zhao,Ting Zhang,Chentingying Zhang,Dali Ding
DOI: https://doi.org/10.1016/j.jallcom.2020.158512
IF: 6.2
2021-05-01
Journal of Alloys and Compounds
Abstract:<p>In the present study, Al-3 wt% Al<sub>2</sub>O<sub>3</sub> master alloy was successfully prepared by the reaction between calcined kaolin and aluminum melt, combined with mechanical stirring and high-energy ultrasonic dispersion technology. The γ-Al<sub>2</sub>O<sub>3</sub> particles produced by the reaction are uniformly dispersed in the matrix, and the average size of γ-Al<sub>2</sub>O<sub>3</sub> is about 65 nm. The refinement effect of Al-3 wt% Al<sub>2</sub>O<sub>3</sub> master alloy on A356 alloy was studied. It was found that the α-Al grain size in A356 alloy refined by Al-3 wt% Al<sub>2</sub>O<sub>3</sub> master alloy was decreased from 980 ± 155 µm to 337 ± 95 µm. Compared with the Al-5Ti-1B master alloy, Al-3 wt% Al<sub>2</sub>O<sub>3</sub> has a higher refinement efficiency. In addition, the refinement efficiency of the Al-3 wt% Al<sub>2</sub>O<sub>3</sub> master alloy will not fade within 60 min. Transmission electron microscope analysis showed that the orientation relationship between γ-Al<sub>2</sub>O<sub>3</sub> and Al was (22−2)<sub>γ-Al2O3</sub>[011]<sub>γ-Al2O3</sub>//(11−1)<sub>Al</sub>[011]<sub>Al</sub>, which demonstrated that γ-Al<sub>2</sub>O<sub>3</sub> could be used as heterogeneous nucleation sites to refine α-Al grains. Moreover, the tensile properties of A356 alloy had been significantly improved.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering