Abstract:Ion beam-assisted deposition (IBAD) has been proposed as a promising texturing technology that uses the film epitaxy method to obtain biaxial texture on a non-textured metal or compound substrate. Magnesium oxide (MgO) is the most well explored texturing material. In order to obtain the optimal biaxial texture, the actual thickness of the IBAD-MgO film must be controlled within 12nm. Due to the bombardment of ion beams, IBAD-MgO has large lattice deformation, poor texture, and many defects in the films. In this work, the solution deposition planarization (SDP) method was used to deposit oxide amorphous Y2O3 films on the surface of Hastelloy C276 tapes instead of the electrochemical polishing, sputtering-Al2O3 and sputtering-Y2O3 in the commercialized buffer layer. An additional homogeneous epitaxy MgO (epi-MgO) layer, which was used to improve the biaxial texture in the IBAD-MgO layer, was deposited on the IBAD-MgO layer by electron-beam evaporation. The effects of growth temperature, film thickness, deposition rate, and oxygen pressure on the texture and morphology of the epi-MgO film were systematically studied. The best full width at half maximum (FWHM) values were 2.2° for the out-of-plane texture and 4.8° for the in-plane texture for epi-MgO films, respectively. Subsequently, the LaMnO3 cap layer and YBa2Cu3O7-x (YBCO) functional layer were deposited on the epi-MgO layer to test the quality of the MgO layer. Finally, the critical current density of the YBCO films was 6 MA/cm2 (77 K, 500 nm, self-field), indicating that this research provides a high-quality MgO substrate for the YBCO layer.

Forty-five Degree Oriented YBa2Cu3O7−x/MgO Interface Structures Studied by High-Resolution Electron Microscopy

Intrinsic structure and thermal stability of YBCO thin film

Microstructure of Epitaxial YBa2Cu3O7−δ Thin Films Grown on Pb(Mg1/3Nb2/3)0.7Ti0.3O3 Substrates

Structural and electronic properties of epitaxial YBaCuO/LaCaMnO bilayers grown on SrTiO$_3$ (110) substrates

Structural characterization of YBa(2)Cu(3)O(7)/Y(2)O(3) composite films

Microstructures of YBa1.85Eu0.15Cu3O7− Superconducting Films Grown on SrTiO3 and YSZ Substrates

Growth of Cubic MgxZn1-xO Films and Characterization

Microstructural Features at the Interface Between Laser Ablated YBa2Cu3O7 Films and LaAlO3 Substrates

Microstructure and Growth of the Epitaxial Superconducting YBa2Cu3O7 Films

Microstructure and Interfaces Investigations of Yba2cu3o7/Prba2cu3o7 Superlattices by Hrtem

Microstructural characterization of YBa2Cu3O7-x thin films grown on Y-ZrO2

Transmission Electron Microscopy Study of YNi2B2C Thin Film Growth on MgO(001)

CeO 2 [100]∥MgO[100]in-plane Epitaxy for Bi-epitaxial Grain Boundary Junctions

TEM STUDY OF THE MICROSTRUCTURE AND INTERFACES IN YBa2Cu3Oy THIN FILMS GROWN ON SILICON WITH A Eu2CuO4/Y-ZrO2 BI-LAYER BUFFER

Highly heteroepitaxial thin films of YBa2Cu3Oy grown on silicon with Eu2CuO4/Y-ZrO2 bi-layer buffer

Cross-sectional TEM studies of YBa2Cu3O7-x superlattices

Untwinned YBa$_2$Cu$_3$O$_{7-δ}$ thin films on MgO substrates: a platform to study strain effects on the local orders in cuprates

Formation and Characterization of YBa2Cu3O7−δ High-Tc Thin Films by MOCVD with Single Mixed Precursor

Dominant Effect of Oxygen Enhancement on the Crystalline Orientation of Yba2cu3ox Film Prepared by Liquid-Phase Epitaxial Growth

Transmission Electron Microscopy and High-Resolution Electron Microscopy Study of YNi<sub>2</sub>B<sub>2</sub>C Thin Film on Y<sub>2</sub>O<sub>3</sub>-Buffered MgO

Preparation of MgO Self-Epitaxial Films for YBCO High-Temperature Coated Conductors