Effect of Heat Treatment on Microstructure and Mechanical Properties of Laser Melting Deposited High Temperature Titanium Alloy Ti60A

MA Taoran,TANG Haibo,FANG Yanli,WANG Huaming

DOI: https://doi.org/10.3969/j.issn.1001-3814.2012.14.059

2012-01-01

Abstract:Laser melting deposition was utilized to shape the near-alpha high temperature titanium alloy Ti60A thick plate.The forming mechanism of solidified structures was investigated.The results show that the laser deposited Ti60A alloy consists of columnar grains growing directionally along the deposited direction,and fine basket weave transformed β phase are uniformly distributed within the grain.Microstructure and mechanical properties of the alloy were systematically studied while double-annealing treatment was applied in upper α+β phase field and α phase.The results show that the double annealing for the alloy leads to a unique and stable bi-model microstructure consisting of crab-claw-like primary α phase and thin lamellar transformed β phase.Moreover,decreasing the annealing temperature of first step can diminish continuous grain boundary α phase.As the remaining β phase,produced by double annealing,displayed better plastic performance during tensile tests,the plastic property of the alloy improves.