(Zn,Ca) Solid-Solution Behavior and Luminescence Properties of Ca_(1-x)Zn_xTiO_3∶0.002Pr~(3+) Phosphors

洪樟连,张朋越,王民权

2005-01-01

Abstract:Nominal composition of Ca_(1-x)Zn_xTiO_3∶0.002Pr~(3+)(x=0.0～～0.20) phosphors were prepared by conventional solid reaction route,the solid-solution structure and luminescence properties of Zn-doped Ca_(1-x)Zn_xTiO_3∶0.002Pr~(3+) phosphors were investigated by XRD and PL measurements,the effect of solid-solution structure formed by substitution between Ca~(2+) and Zn~(2+) ions was analyzed.The results reveal that with the increase of Zn substitution content below 0.01,lattice parameters and the intensity of excitation peak at both 260 and 330nm as well as the corresponding 610 nm emission intensity are monotonously decreased quickly in a similar tendency.Furthermore,the evolution of luminescence intensity and crystal cell parameters against Zn doping concentration are in good agreement.Above results are closely related with the structure evolution within Ca_(1-x)Zn_xTiO_3∶ 0.002Pr~(3+) solid-solution phase formed by the Zn ions substitution for the Ca sites.Present study reveals that the solid-solution structure formed by substitution between Ca~(2+) and Zn~(2+) ions has significant effect on luminescence properties of single Ca_(1-x)Zn_xTiO_3∶0.002Pr~(3+) phase.