Electrochemical Characteristics and Intercalation Mechanism of ZnS/C Composite As Anode Active Material for Lithium-Ion Batteries

Li He,Xiao-Zhen Liao,Ke Yang,Yu-Shi He,Wen,Zi-Feng Ma

DOI: https://doi.org/10.1016/j.electacta.2010.11.014

2008-01-01

Abstract:ZnS/C composites were synthesized by a combined precipitation with carbon coating method. Morphology and structure of the as-prepared ZnS/C composite materials with carbon content of 4.6 wt%, 9.3 wt% and 11.4 wt% were characterized using TEM and XRD technique. TEM observation demonstrated that the ZnS/C (9.3 wt% C) composite showed excellent microstructure with 20–30 nm ZnS nanoparticles uniformly dispersed in conductive carbon network. Electrochemical tests showed that the ZnS/C (9.3 wt% C) composite presented superior performance with initial charge and discharge capacity of 1021.1 and 481.6 mAh/g at a high specific current of 400 mA/g, after 300 cycles, the discharge capacity of ZnS/C electrode still maintained at 304.4 mAh/g, with 63.2% of its initial capacity. The rate capability and low temperature performance of the ZnS/C (9.3 wt% C) composite were compared with commercial MCMB anode. The results showed that the ZnS/C (9.3 wt%) composite exhibited much better cycle capability and low temperature performance than MCMB anode. ZnS/C composite seems to be a promising anode active material for lithium ion batteries. Intercalation mechanism of the ZnS/C composites for lithium ion insertion–extraction is proposed based on the ex situ X-ray diffraction analysis incorporating with its electrochemical characteristics.