Thermal and Mechanical Properties of Polyurethane/montmorillonite Nanocomposites Based on a Novel Reactive Modifier

JW Xiong,YH Liu,XH Yang,XL Wang
DOI: https://doi.org/10.1016/j.polymdegradstab.2004.07.001
IF: 5.204
2004-01-01
Polymer Degradation and Stability
Abstract:Polyurethane/montmorillonite (PU/MMT) nanocomposites based on thermally stable, aromatic amine modifier containing active groups (methylene-bis-ortho-chloroanilline, MOCA) were synthesized by intercalative polymerisation. The cured hybrid exhibited higher thermal stability and better mechanical strength than pure polyurethane or polyurethane/cetyltrimethyl-ammonium-bromide (CTAB)-modified MMT (PU/C16-MMT). The moduli and the onset degradation temperature for the PU were obviously increased by addition of MMT treated with the MOCA (MO-MMT), and the mechanical strength was dramatically increased by about 600% for the MO-MMT only increased by about 450% for the C16-MMT at the point of 5wt% organically modified MMT content. Surprisingly, the glass transition temperature of the PU/organic-MMT nanocomposites was lower than that of the PU.
What problem does this paper attempt to address?