Abstract:Cold-drawn pearlitic steel wires have the highest strength of all steel products. It is a promising way to enhance the mechanical properties by increasing the carbon content. However, the proeutectoid cementite forms easily due to the hypereutectoid composition and deteriorates the mechanical and processing properties of steel wires. It is important for hypereutectoid steel wire drawing to achieve a fine and fully pearlitic microstructure without proeutectoid cementite. The austenitization and following continuous cooling process were simulated in the dilatometer for a hypereutectoid steel. The microstructure was observed with OM and SEM. The transformation temperature, prior-austenite grain size, pearlitic interlamellar spacing and proeutectoid cementite thickness were determined by dilatometric curves or OM/SEM images. The austenite grain size increases rapidly with a higher temperature and almost keeps invariant with a longer austenitization time. Faster cooling rate, higher austenitization temperature or longer austenitization time decrease the starting and finishing temperature of phase transformation, widen the temperature range, refine the pearlitic interlamellar spacing and suppress the proeutectoid cementite precipitation (reduce the thickness or make it discontinuous). However, it is easy to form martensite which is bad for the homogeneity of pearlitic microstructure by increasing the cooling rate or austenitization temperature simply. A fine pearlite in a pseudoeutectoid microstructure is achieved by extending the austenitization time to 60 min and controlling the austenitization temperature and cooling rate. Discontinuous proeutectoid cementite is observed in the samples with the higher austenitization temperature. Higher austenitization temperature and longer time are helpful to weaken the carbon concentration gradient. The homogeneous carbon distribution restrains carbon diffusion for cementite nucleation during the proeutectoid cementite precipitation and pearlite transformation, which decreases the transformation temperature. Compare to pearlite transformation, the proeutectoid cementite precipitation is affected more strongly by the carbon diffusion due to a longer diffusion distance. Therefore, the precipitation amount of proeutectoid cementite is reduced if the carbon diffusion is restrained. The amount of grain corner and grain edge reduce more dramatically than that of grain boundary if austenite grain size increases. The proeutectoid cementite only nucleates in grain corner and grain edge. The pearlite nucleation can form in grain boundary. Therefore, the larger austenite grains result in the sharp reduction in the sites for nucleation of proeutectoid cementite. Then, the amount of proeutectoid cementite are reduced and the morphology becomes discontinuous.

Influence of Undercooling on Dynamic Transformation and Microstructure Evolution in Eutectoid Steel

INFLUENCE OF DEFORMATION TEMPERATURE ON THE MICROSTRUCTURE TRANSFORMATION IN MEDIUM CARBON STEEL

Microstructure Refinement Mechanism of Undercooled Cu55Ni45 Alloys

Microstructural evolution during the austenite-to-ferrite transformation from deformed austenite

Dynamic continuous cooling transformation, microstructure and mechanical properties of medium-carbon carbide-free bainitic steel

Non-equilibrium solidification of bulk undercooled Ni–P eutectic alloys

Effect of Minor Addition of Co on Nonequilibrium Solidification of Deeply Undercooled Cu Based Alloys

EFFECTS OF AUSTENITIZATION AND COOLING RATESON THE MICROSTRUCTURE IN A HYPER-EUTECTOID STEEL

Effect of Transformation Temperature on the Ferrite–Bainite Microstructures, Mechanical Properties and the Deformation Behavior in a Hot-Rolled Dual Phase Steel

Effect of Deformation and Cooling Rate on the Transformation Behavior and Microstructure of X70 Steels

New Microstructural Features Occurring During Transformation from Austenite to Ferrite under the Kinetic Influence of Magnetic Field in A Medium Carbon Steel

Effects of austenitization and cooling rates on the microstructure in a hypereutectoid steel

Effect of Hot Coiling Under Accelerated Cooling on Development of Non-equiaxed Ferrite in Low Carbon Steel

A THEORETICAL ANALYSIS ON EFFECT OF DEFORMATION ABOVE Ae3 TO THE NUCLEATION OF PROEUTECTOID FERRITE TRANSFORMATION

Influence of Deforming Temperatures on the Strain Induced Transformation in Q235 Plain Carbon Steel

Re-Examination of the Microstructural Evolution in Undercooled Co-18.5at.%B Eutectic Alloy

Atom-probe tomographic and dilatometric studies of phase-transformations after inter-critical annealing of a low-carbon dual-phase steel

The austenite to polygonal ferrite transformation in low-alloy steel: multi-phase-field simulation

Microstructural Evolution and Kinetics for Post-dynamic Transformation in a Plain Low Carbon Steel

Effect of strain path on dynamic strain-induced transformation in a microalloyed steel

Effect of the cooling rate in the medium temperature zone on the phase transformation and microstructure of carbide-free bainitic steel