Abstract:Well-aligned ZnO nanowires were hydrothermally synthesized based on a facile method for preparing the ZnO seed layer which was derived from the combination of a sol—gel process and the spin-coating technique. The effect of the contents of growth solution and the growth duration on the morphology of ZnO nanowires has been investigated. The results indicated that long and vertically aligned ZnO nanowires could be obtained by adjusting the contents of ammonia and polyethyleneimine (PEI) in the growth solution. Under the optimized condition, the length of ZnO nanowires increased fast and almost linearly with the growth duration. After 10 h incubation, ZnO nanowires more than 25 μm in length were obtained. By combining the conventional photolithographic method with this hydrothermal approach, long and well-aligned ZnO nanowire arrays were selectively grown on the substrate. In addition, the bottom fusion at the foot of the nanowires has been obviously improved. The results demonstrated that the improved hydrothermal process is favorable to synthesize long and well-aligned ZnO nanowires, and possesses good process compatibility with the conventional photolithographic technique for preparing ZnO nanowire arrays. So it has great potential in applications such as display and field emission devices.

Seed-layer controlled synthesis of well-aligned ZnO nanowire arrays via a low temperature aqueous solution method

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Growth of Arrayed ZnO Nanowires Using a Solution Method

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Seed Free Growth of Aligned ZnO Nanowire Arrays on AZO Substrate

Controlled Growth of Well-Aligned Zno Nanowire Arrays Using the Improved Hydrothermal Method

Controllable Synthesis of Vertically Aligned ZnO Nanorod Arrays in Aqueous Solution.

Facile route to well-aligned ZnO nanowire arrays

Controllable Growth of Well-Aligned Zno Nanorod Arrays by Low-Temperature Wet Chemical Bath Deposition Method

Synthesis of Well-aligned ZnO Nanowires Using Simple Physical Vapor Deposition Without Catalysts or Additives

Patterned growth of vertically aligned ZnO nanowire arrays on inorganic substrates at low temperature without catalyst.

Patterned growth of vertically aligned ZnO nanowire arrays on inorganic substrates at low temperature without catalyst

Selective Growth of Vertical-aligned ZnO Nanorod Arrays on Si Substrate by Catalyst-free Thermal Evaporation

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

Controlled Growth of ZnO Nanorods and Nanotubes by Chemical Method on Electrodeposited Seed Layer

A Low-Temperature Aqueous Solution Route to Large-Scale Growth of Zno Nanowire Arrays

Controllable Hydrothermal Synthesis of ZnO Nanowires Arrays on Al-doped ZnO Seed Layer and Patterning of ZnO Nanowires Arrays Via Surface Modification of Substrate

Controlled Growth of Well-Aligned Hierarchical ZnO Arrays by a Wet Chemical Method

One step synthesis of vertically aligned ZnO nanowire arrays with tunable length

General Route to Zno Nanorod Arrays on Conducting Substrates Via Galvanic-Cell-Based Approach

Synthesis of Vertical Arrays of Ultra Long ZnO Nanowires on Noncrystalline Substrates