Abstract:Ti(IV) polycation-intercalated niobate was synthesized through a stepwise ion-exchange route, in which HNb3O8 was used as the layered host, n-decylamine as a preswelling agent, and tetrabutyl titanate (abbreviated to TBT) as a titanium source. After the Ti(IV) polycation-intercalated niobate was calcined at 723 K in air environment, TiO2-pillared HNb3O8 was given. X-ray diffraction (XRD), framework infrared spectra FT-IR, N-2 adsorption-desorption technique and transmission electron microscopy (TEM) were employed to investigate the structure of the obtained products. Characterizations by XRD and N2 adsorption-desorption isotherms indicated that the TiO2-pillared HNb3O8 was a porous layered material with an interlayer distance (d(010)) of 1.39 nm, a pillar height of 0.63 nm and a BET specific surface area of 35 m 9 The TiO2-Pillared solid was thermally very stable, and its layered structure could be retained up to 823 K. Combined with our previous studying work, it was found that TBT as well as titanium tetraisopropoxide (abbreviated as TIP) could be used as the precursor of TiO2 pillars. Apparently, the TBT is more practicable than TIP since the latter is very costly and the former relatively cheap. It was demonstrated that the Ti(IV) polycation intercalated in the interlayers of the layered niobate contain no CH3COO- and other organic groups, and thus it can be inferred that the Ti(IV) polycations have a formula of [Ti(OH)(x)(H2O)(y)](z+), in which x, y, and z are variables.

Synthesis of Calcium Titanate from [ca(h2o)3]2[ti2(o2)2o(nc6h6o6)2]·2h2o As a Cheap Single-Source Precursor

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Hydrothermal Synthesis and Photocatalytic Property of CaTiO_3 Assisted with Sodium Citrate

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Hydrothermal synthesis and photocatalytic property of CaTiO 3 assisted with sodium citrate

Template-free Hydrothermal Synthesis of Macroporous TiO2 Microspheres on a Large Scale

Method for preparing CaTi2O4(OH)2 nanolayer

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

A Simple Solvothermal Process to Synthesize CaTiO3 Microspheres and Its Photocatalytic Properties

Controllable Synthesis of Cati2o4(Oh)(2) Nanoflakes by A Facile Template-Free Process and Its Properties

Preparation of Tio2-Pillared Hnb3o8: Tetrabutyl Titanate Used As A Cheap Titanium Source

Facile and large-scale synthesis of hollow TiO2 nanostructures from TiCl3 solution

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

A facile synthesis of hierarchical TiO2 for dye adsorption and photocatalysis

Ba 4 Ti 13 O 30 Nanocrystals Prepared by Hydrothermal Method

Synthesis of Nanoparticles of the Giant Dielectric Material, CaCu3Ti4O12 from a Precursor Route

Low-Cost Synthesis of Titanium Silicalite-1 (TS-1) with Highly Catalytic Oxidation Performance through a Controlled Hydrolysis Process

Hydrothermal synthesis of hierarchical titanium silicalite-1 using single template

Controllable Synthesis of Tio2 Single Crystals with Tunable Shapes Using Ammonium-Exchanged Titanate Nanowires As Precursors

Dissolution/recrystallization Growth of Titanate Nanostructures by Amorphous Precursor