Abstract:Under the background of fossil fuel depletion and global warming, the large amount of carbon dioxide (CO 2 ) produced by industrial production was a renewable, clean and natural C1 feedstock that was becoming an ideal feedstock to produce value-added chemicals. The synthesis of non-isocyanate polyurethanes (NIPU) from cyclic carbonates as intermediate products was a typical way to realize the efficient recycling of CO 2 . To improve the low carbonization, flammability and poor mechanics of NIPU and expand its application scenarios, the NIPU was synthesized from biological cardanol and CO 2 by a relatively green synthesis route, and modified by flame retardants containing different valence phosphorus. Compared with ECH-CarCO 2 -HMDA, the char residue of PO-CarCO 2 -HMDA and PP-CarCO 2 -HMDA increased by 248.8 % and 172.7 % respectively under nitrogen atmosphere, and 345.7 % and 151.9 % respectively under air atmosphere. More importantly, the peaks of heat release rate of modified NIPUs were reduced by 30.0 % and 18.4 %, and their total heat release were decreased by 15.2 % and 10.4 %, respectively. After various characterization analysis, this was mainly due to the generation of heat-stable structure containing phosphorus and oxygen during the burning process. Simultaneously, the toughness of PO-CarCO 2 -HMDA and PP-CarCO 2 -HMDA increased by 261.0 % and 105.1 %. In addition, the synthetic NIPU as an adhesive in different materials was also explored, and the adhesion strength can reach 2.47 MPa. This study provided a new idea for preparing bio-based NIPU which was more widely used.

Preparation and properties of all-bio-based non-isocyanate polyurethane

Preparation of Non-Isocyanate Polyurethanes from Mixed Cyclic-Carbonated Compounds: Soybean Oil and CO2-Based Poly(ether carbonate)

Synthesis and Characterization of Cardanol-Based Non-Isocyanate Polyurethane

Simultaneous Interpenetrating Polymer Networks of Polyurethane from Pentaerythritol–Modified Castor Oil and Polystyrene: Structure–Property Relationships

Carbodiimide-Assisted Synthesis of High Purity Bis(cyclic carbonate) Under Atmospheric Conditions for Preparation of Non-Isocyanate Polyurethane

Mechanically strong non-isocyanate polyurethane thermosets from cyclic carbonate linseed oil

Synthesis, Characterization and Properties of Soybean Oil-Based Polyurethane

Progress in Study of Non-Isocyanate Polyurethane

Bio-based epoxy/polyurethane interpenetrating polymer networks (IPNs) derived from plant oils with tunable thermal and mechanical properties

Mechanical Properties of Polyurethane Foams Prepared from Liquefied Corn Stover with PAPI.

Catalytic Synthesis of Carbonated Soybean Oil

Innovative design and green synthesis of bio-based non-isocyanate polyurethanes: Efficient combination of cardanol and carbon dioxide with high fire safety and robust adhesion

Synthesis and characteristics of nonisocyanate polyurethane composed of bio‐based dimer diamine for supercritical CO2 foaming applications

New biobased high functionality polyols and their use in polyurethane coatings

Polylactide-Based Nonisocyanate Polyurethanes: Preparation, Properties Evaluation and Structure Analysis

Synthesis Of Soy-Polyols Using A Continuous Microflow System And Preparation Of Soy-Based Polyurethane Rigid Foams

Carbon Nanofibers Reinforced Soy Polyol-Based Polyurethane Nanocomposites

Preparation and Characterization of Novel Rigid Polyurethane Foams by Epoxidized Soybean Oil

Synthesis of non‐isocyanate polyurethanes with high‐performance and self‐healing properties

Polyurethane Rigid Foams Formed from Different Soy-Based Polyols by the Ring Opening of Epoxidised Soybean Oil with Methanol, Phenol, and Cyclohexanol