Abstract:Abstract In this study, low-temperature fired CaMg 1− x Li 2 x Si 2 O 6 microwave dielectric ceramics were prepared via the traditional solid-state reaction method. In this process, 0.4 wt% Li 2 CO 3 -B 2 O 3 -SiO 2 -CaCO 3 -Al 2 O 3 (LBSCA) glass was added as a sintering aid. The results showed that ceramics consisted of CaMgSi 2 O 6 as the main phase. The second phases were CaSiO 3 always existing and Li 2 SiO 3 occurring at substitution content x > 0.05. Li + substitution effectively lowered sintering temperature due to 0.4 wt% LBSCA and contributed to grain densification, and the most homogeneous morphology could be observed at x = 0.05. The effects of relative density, the second phase, and ionic polarizability on dielectric constant (ε r ) were investigated. The quality factor ( Q × f ) varied with packing fraction that concerned the second phase. Moreover, the temperature coefficient of the resonant frequency (τ f ) was influenced by MgO 6 octahedral distortion and bond valence. Excellent dielectric properties of the CaMg 1− x Li 2 x Si 2 O 6 ceramic was exhibited at x = 0.05 with ε r = 7.44, Q × f = 41,017 GHz ( f = 15.1638 GHz), and τ f = −59.3 ppm/°C when sintered at 900 °C. It had a good application prospect in the field of low-temperature co-fired ceramic (LTCC) substrate and devices.

Preparation of Low Temperature Cofired CaO-MgO-SiO2 Microwave Ceramics Doped with Additives by Sol-Gel Method

Synthesis and microwave dielectric properties of (Ca0.7Mg0.3)SiO3 nanopowder prepared at low temperature

Influence of CaO content by mass in sintering aid and sintering temperature on the properties of Al2O3-based microwave ceramic materials

Low -temperature sintering of Al2O3 microwave dielectric ceramic doped with CuO-TiO2 gel

Low-Temperature Firing And Microwave Dielectric Properties Of Ca[(Li0.33nb0.67)(0.9)Ti-0.1]O3-Delta Ceramics With Lif Addition

Synthesis and Microwave Dielectric Properties of CaO–MgO–SiO2 Submicron Powders Doped with Li2O–Bi2O3 by Sol–gel Method

Synthesis and Microwave Dielectric Properties of (Ca<SUB>0.7</SUB>Mg<SUB>0.3</SUB>)SiO<SUB>3</SUB>Ceramic by Sol-Gel Process: Synthesis and Microwave Dielectric Properties of (Ca<SUB>0.7</SUB>Mg<SUB>0.3</SUB>)SiO<SUB>3</SUB>Ceramic by Sol-Gel Process

Low-Temperature Sintering and Microwave Dielectric Properties of (ca0.9mg0.1)sio3 Ceramic with Li2co3 Addition

Sintering characteristics and crystallization for sol–gel-derived powders for low-dielectric and low-temperature sintering ceramics

Synthesis and Microwave Dielectric Properties of (Ca_(0.7)Mg_(0.3))SiO_3 Ceramic by Sol-Gel Process

Modification of Low Temperature Sintered CMS Microwave Dielectric Ceramics Doped with Nanopowder

Low-Firing Ba_4(Nd_(0.85)Bi_(0.15))_(28/3)Ti_(18)O_(54) Microwave Ceramics

Mgo-Al2o3-Sio2 Glass-Ceramic Prepared by Sol-Gel Method

A New System of Low Temperature Sintering ZnO–SiO2 Dielectric Ceramics

Preparation and Characterization of CaTiO 3 –(li 1 / 2 Nd 1 / 4 Sm 1 / 4 )tio 3 Microwave Ceramics by a Sol–gel Combustion Process

Low-temperature sintering and phase component modulation of 0.95MgTiO3–0.05CaTiO3 microwave dielectric ceramics

Low-temperature sintering and microwave dielectric properties of CaMg1−xLi2xSi2O6 (x = 0−0.3) ceramics

Microwave Dielectric Properties of Low Temperature Co-Fired Glass–ceramic Based on B2O3–La2O3–MgO Glass with La(Mg0.5Ti0.5)O3 Ceramics

Low-temperature sintering and microwave dielectric properties of LiF-doped CaMg1-xZnxSi2O6 ceramics

Low Temperature Sintering and Microwave Dielectric Properties of Ba4nd9.33ti18o54 Ceramics Doped with Crystallizable Glass

Microwave Dielectric Properties and Low-Temperature Sintering of (zn0.8mg0.2)2sio4–tio2 Ceramics with Li2O–B2O3