Abstract:Uniformly distributed ZnO nanorods have been grown by plasma-enhanced chemical vapor deposition using a two-step process. By controlling the oxygen content in the gas mixture during the nucleation and growth steps, no catalyst is required for the formation of ZnO nanorods. High-resolution transmission electron microscopy studies show that ZnO nanorods are single crystals and that they grow along the c axis of the crystal plane. Alignment of these nanorods with respect to the substrates depends on the lattice mismatch between ZnO and the substrate, the surface electric field, and the amount of defects in the starting nuclei. Room-temperature photoluminescence measurements of these ZnO nanorods have shown ultraviolet peaks at 380 nm with a full width at half-maximum of 106 meV, which are comparable to those found in high-quality ZnO films. Photoluminescence measurements of annealed ZnO nanorods in hydrogen and oxygen atmospheres indicate that the origins of green emission are oxygen vacancies and zinc interstitials, while oxygen interstitials are responsible for the orange-red emission. A mechanism for the nanorod growth is proposed. (C) 2004 American Institute of Physics.

Phase-Segregation Assisted Growth Of Quasi-Aligned Zno Nanorods On A Mg0.6zn0.4o-Coated Si Substrate By Thermal Evaporation

Vapor phase growth and photoluminescence of oriented-attachment Zn2GeO4 nanorods array

Selective Growth of Vertical-aligned ZnO Nanorod Arrays on Si Substrate by Catalyst-free Thermal Evaporation

Growth Mechanism And Properties Of Zno Nanorods Synthesized By Plasma-Enhanced Chemical Vapor Deposition

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Aligned ZnO Nanorod Arrays Fabricated on Si Substrate by Solution Deposition

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Eutectic Condensation and Nucleation in Vapor-Liquid-Solid Grown Zno Nanorod Arrays on Si Substrate

Quasi-aligned Zn1−xMgxO Nanorods Synthesized by Thermal Evaporation

Oriented growth of ZnO nanostructures on Si and Al substrates

Electronic Structure and Optical Properties of Vertically Aligned Zno Nanorod Arrays Grown by Low-Temperature Hydrothermal Method

Low-temperature Growth and Raman Scattering Study of Vertically Aligned ZnO Nanowires on Si Substrate

Synthesis of Zno/Cubic (zn, Mg)O Heterostructure Nanorods

One-Step Growth of Zno from Film to Vertically Well-Aligned Nanorods and the Morphology-Dependent Raman Scattering

Effect of Substrate Temperature on the Growth and Photoluminescence Properties of Vertically Aligned ZnO Nanostructures

Controllable Growth of Well-Aligned Zno Nanorod Arrays by Low-Temperature Wet Chemical Bath Deposition Method

Catalyst-Free Two-Step Growth of Quasialigned Znmgo Nanorods and Their Properties

Synthesis and Raman Analysis of 1D-Zno Nanostructure Via Vapor Phase Growth

Nano/Micro-Structured ZnO Rods Synthesized by Thermal Chemical Vapor Deposition with Perpendicular Configuration

Synthesis of Ordered ZnO Nanorods Film on Zinc-Coated Si Substrate and Their Photoluminescence Property

Effects of Substrate on the Structure, Morphology and Optical Properties of Vertically Aligned Zno Nanorod Arrays Grown by Low-Temperature Cbd Method