Abstract:Mordenite composite membranes were prepared by means of coating a porous α-alumina support with nanosized mordenite seeds followed by hydrothermal crystallization. A systematic investigation was performed on the influence of several factors such as ageing of the reaction mixture, alkalinity, salt addition and temperature on the formation of a mordenite membrane on the seeded support. The ageing of the reaction mixture reduces the growth rate of mordenite crystal along a-axis and b-axis but hardly influences the growth rate along c-axis. As a result, the boundaries between the surface crystals become a little larger with prolonging the period of ageing time. The growth rate of the mordenite crystal along individual axes increases first and then decreases with increasing concentration of sodium hydroxide. A higher alkalinity is unfavorable for the formation of a continuous mordenite membrane. The addition of salt in the reaction mixture has different effect on the growth rate of the mordenite crystal along each axis. With increasing the amount of salt, there was hardly influence on the growth rate along c-axis, whereas an obvious decline was observed in the growth rate along either a-axis or b-axis, which enlarges the boundaries between the surface crystals. The growth rate of the mordenite crystal increases more along c-axis than that along a-axis or b-axis with increasing temperature for hydrothermal crystallization. The use of a temperature as high as 473 K produces a membrane composed of bar-like crystals with larger boundaries.

Al2O3–SiO2–TiO2 Composite Ceramic Membranes from Sol–gel Processing

Preparation and structure of Al2O3-SiO2-TiO2 composite ceramic membranes

Preparation and Characterization of Al2O3-Based Composite Membranes by Sol-Gel Method

Preparation and Characterization of Al<sub>2</sub>O<sub>3</sub>-Based Composite Membranes by Sol-Gel Method

AFM study on surface morphology of Al2O3SiO2TiO2 composite ceramic membranes

Preparation of Mordenite Composite Membranes with Seeding

Characterization, performance analysis and comparison of ZrO2 or TiO2 doped Al2O3 composite membranes using sol-gel technique

Preparation and Modification of Ceramic Membrane and Its Application in Oil/Water Wastewater Treatment

In-situ Grown Columnar Mullite Reinforced SiC Porous Ceramic Membrane Support with Excellent Mechanical Performance and Corrosion Resistance: Using TiO2 As the Key to Form Columnar Mullite

Preparation of a High-Performance Porous Ceramic Membrane by a Two-Step Coating Method and One-Step Sintering

Study on surface morphology of porous ceramic membranes

Preparation of defect free ceramic/Ti composite membranes by surface modification and in situ oxidation

Effects of Substrates on Ceramic Composite Membrane

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes

Morphological Characterization of γ-Al 2 O 3 Membranes Fabricated from Ammonium Aluminum Sulphate

Supported mesoporous SiO2 membrane synthesized by sol–gel-template technology

A high-stability silica-clay composite: synthesis, characterization and combination with TiO2 as a novel photocatalyst for Azo dye.

Preparation and properties of Al2O3/Al-2(1-0.2)Mg0.2Ti(1+0.2)O5 matrix ceramic composite

Asymmetric alumina-based ultrathin composite ceramic membranes with interfacial modification of black talc nanosheets

Sol-gel Derived Zirconia Membrane on Silicon Carbide Substrate