Abstract:Ultrafine-grained Al–Mg–Si alloys with four different Mg/Si ratios (=0.75, 1.10, 1.48, and 1.94) were prepared by using extrusion and cold-drawing. The microstructural evolution during aging treatment was examined by using transmission electron microscopy. Hardness and electrical conductivity of the alloys were, respectively, measured before and after aging treatment. Experimental results showed that \( \beta^{\prime\prime} \) precipitates were dispersed within the grain interior in all the four aged alloys. Although the precipitate size was insensitive to the Mg/Si ratio, the precipitate number density as well as the inter-precipitate spacing was greatly dependent on the Mg/Si ratio. The optimized Mg/Si ratio within present work was 1.48, which led to the densest precipitation, and resulted in the highest hardness and simultaneously greatest conductivity. These findings are rationalized by considering the precipitation behaviors in the ultrafine-grained length scale and their effect on the hardness–conductivity relationship. A strengthening model was proposed for the ultrafine-grained Al–Mg–Si alloys, which accounted for the multiple contributions from grain size, dislocations, solid solution atoms, and precipitates to the hardness. The calculations were in good agreement with the experimental results. Similarly, the effect of multiple microstructural features on the electrical conductivity was also quantitatively described by adopting a model. The contribution of precipitation to both the hardness and conductivity is well demonstrated for the ultrafine-grained Al–Mg–Si alloys, which will be helpful for material design of advanced ultrafine-grained Al alloys with enhanced performance.

Precipitation behavior and damping characteristic of Mg–Al–Si alloy

Damping Capacity Associated with Precipitation in Mg2Si/Mg–9Al Composite Materials

Effect of a Trace Addition of Sn on the Aging Behavior of Al–Mg–Si Alloy with a Different Mg/Si Ratio

Effect of Aging Treatment on Microstructure and Damping Properties of Mg-Al-Ca-Mn-Zn Alloy

Study on properties and precipitation behavior of 6000 series alloys with high Mg/Si ratios and Cu contents

Influence of Mg Contents on Aging Precipitation Behavior of Al–3.5Cu–xMg Alloy

The natural aging and precipitation hardening behaviour of Al-Mg-Si-Cu alloys with different Mg/Si ratios and Cu additions

Tensile properties and fracture behavior of Al–8Si alloy sheets with different Mg under natural aging

Precipitates evolution and strengthening of Al–Mg2Si alloys containing high-Cu contents during ageing process

Low Frequency Damping Capacities and Mechanical Properties of Mg–Si Alloys

Investigation of Precipitation Strengthening Behavior of Al-Mg-Si Alloy Using SAXS

The effects of Ti on the precipitation evolution and age-hardening behavior of Al–7Si–Mg alloy

Microstructure and damping properties of Mg–Si binary hypoeutectic alloys

Precipitation Behavior and Hardening Effects of Si-containing Dispersoids in Al–7Si–Mg Alloy During Solution Treatment

Aging temperature effects on microstructure and mechanical properties for additively manufactured AlSi10Mg

Hot deformation behaviour and microstructure evolution of Al-3%Mg2Si alloy

Influence of Mg content on ageing precipitation behavior of Al-Cu-Li-x alloys

Effect of multi-stage aging on the precipitation strengthening and mechanical properties for an Al-Mg-Si-Ag alloy

Effect of Mg/Si Ratio on the Microstructure and Hardness–conductivity Relationship of Ultrafine-Grained Al–Mg–Si Alloys

The characteristic of damping peak in Mg–9Al–Si Alloys

Precipitation Behavior and Mechanical Performances of A356.2 Alloy Treated by Al–Sr–La Composite Refinement-Modification Agent