Fabrication of Copper-Terephthalate Frameworks and N-Doped Carbon Dots Composite for Boosting Photocatalytic Performance
Thuong-Quang Tran,Hong-Minh Tran,Xuan-Truong Nguyen,Duc-Trung Nguyen,Phuong-Ly Thi Giang,Ngoc-Tue Nguyen
DOI: https://doi.org/10.1007/s11244-022-01732-0
IF: 2.781
2022-11-06
Topics in Catalysis
Abstract:This paper revealed the changes in physical properties, morphology and photocatalytic activity of samples in each stage of the synthesis of during the NCD/CuBDC. Nitrogen-containing Carbon quantum dots, abbreviated as NCD, was used to modify CuBDC, a copper-based metal–organic framework. CuBDC and NCD/CuBDC samples were successfully prepared by an ultrasonic-assisted, solvothermal method from Copper (II) oxide. SEM images demonstrated that the morphology of the materials changed from agglomerating nanospheres to stacked layers. NCD/CuBDC had a greater surface area (23.4 m 2 g −1 ) and pore size (58.39 nm) than CuBDC (18.1 m 2 g −1 ; 29.29 nm) in terms of porous characteristics. NCD/CuBDC was more visible-light-sensitive, with an estimated band gap energy of roughly 2.67 eV. Furthermore, introducing NCDs into MOF structure boosted the material's photoactivity and impeded electron–hole recombination, as evidenced by the increased MB degradation efficiency. The optimal sample was 280-NCD/CuBDC, with the ability to completely process MB within 90 min, while CuO and pristine CuBDC can only degrade around 20% of MB concentration. Additionally, the 280-NCD/CuBDC could be reused five times continuously. The main contributors to the degradation of MB were hydroxyl radicals and photogenerated holes. The formation of 280-NCD/CuBDC catalyst had been suggested based on the results of XRD, FTIR, UV–vis DRS, and SEM images. In the future, the NCD/CuBDC material will be further studied and applied to treat some other types of pollutant compounds present in wastewater such as heavy metals, antibiotics or pesticides.
chemistry, physical, applied