Abstract:The effect of Al substitution for Fe on crystal structure, magnetostriction and spontaneous magnetostriction, anisotropy and spin reorientation of a series of polycrystalline Tb0.3Dy0.7(Fe1−xAlx)1.95 alloys (x = 0, 0.05, 0.1, 0.15, 0.20, 0.25, 0.30, 0.35) at room temperature and 77 K was investigated systematically. It was found that the primary phase of Tb0.3Dy0.7(Fe1−xAlx)1.95 is the MgCu2-type cubic Laves phase structure when x < 0.4 and the lattice constant a of Tb0.3Dy0.7(Fe1−xAlx)1.95 increases approximately and monotonically with the increase of x. The substitution of Al leads to the fact that the magnetostriction λ inceases slightly in a low magnetic field (H ⩽ 40 kA/m), but decreases sharply and is easily close to saturation in a high applied field as x increases, showing that a small amount of Al substitution is beneficial to a decrease in the magnetocrystalline anisotropy. It was also found that the spontaneous magnetostriction λ111 decreases greatly with x increasing. The analysis of the Mössbauer spectra indicated that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry with the changes of composition and temperature, namely spin reorientation. A small amount of non-magnetic phase exists for x = 0.15 in Tb0.3Dy0.7(Fe1−xAlx)1.95 alloys and the alloys become paramagnetic for x > 0.15 at room temperature, but at 77 K the alloys still remain magnetic phase even for x = 0.2. At room temperature and 77 K, the hyperfine field decreases and the isomer shifts increase with Al concentration increasing.

Structure and magnetostriction of Tb1−xPrxFe1.93B0.15 alloys

Synthesis and magnetostriction of TbxPr1−x(Fe0.8Co0.2)1.9 cubic Laves alloys

High Pr-content (Tb0.2Pr0.8)(Fe0.4Co0.6)1.93−xBx magnetostrictive alloys

Structure and magnetostriction of Tb0.36Dy0.64(Fe0.85 Co0.15)2-xBx alloys

Magnetics, Magetostriction, and Spin Reorientation of Tb0.3dy0.6pr0.1(Fe1-Xalx)(1.95) Alloys with Substitution of Fe by Al

Magetostriction, Spin Reorientation and Mossbauer Effect Studies of Tb0.3dy0.7-Xprx(Fe0.9al0.1)(1.95) Alloys

Structure and Magnetostriction of Dy 0.9-X Tb X Pr 0.1 Fe 1.85 and Dy 0.9-X Tb X Pr 0.1 (fe 0.95 Al 0.05 ) 1.8 Alloys

Alloys with Substitution of Fe by Al

A Study of Magnetostriction, Spin Reorientation, and Mössbauer Spectra of Tb 0.3 Dy 0.6 Pr 0.1 (fe 1− X Al X ) 1.95 Alloys with Substitution of Fe by Al

Structure and magnetic properties of mechanically alloyed Tb0.7Pr0.3(Fe0.9B0.1)1.93 and the magnetostriction of its epoxy composites

Magnetostrictive Properties of Tbx(Pr0.5Nd0.5)1−xFe1.93 Cubic Laves Alloys

Magnetostriction of Dy0.6Tb0.3Pr0.1(Fe0.95Mn0.05)x Alloys (1.80 ≤ × ≤ 1.95)

A magnetic, magnetostrictive and Mössbauer study of Tb0.3Dy0.7-xPrx(Fe0.9Al0.1)1.95 alloys

High-pressure Synthesis of Giant Magnetostrictive PrxTb1−xFe1.9 Alloys

Microstructure and Magnetostriction of (dy0.7tb0.3)1−xprxfe1.85 and (dy0.7tb0.3)0.7pr0.3fey Alloys

Synthesis and Magnetostriction of Melt-Spun Pr1−xTbx(Fe0.6Co0.4)2 Alloys

Synthesis and Magnetic Properties of Pr(Fe 1-X Co X ) 2 and Pr 1-Y Tb Y (fe 0.4 Co 0.6 ) 2 Alloys

Structure and magnetic properties of magnetostrictive compounds Tb0.36Dy0.64(Fe0.85Co0.15)2-xBx (0≤x≤0.15)

Magnetism， Magetostriction， and M?ssbauer Effect Studies of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 Alloys

Structure, Spin Reorientation and Mössbauer Effect Studies of Tb 0.3 Dy 0.7 (fe 1− X Al X ) 1.95 Alloys

Structure and Magnetostriction of (dy0.6tb0.3pr0.1)(fe0.95−xmn0.05gax)1.85 Alloys