Self-assembled Nafion–silica nanoparticles for elevated-high temperature polymer electrolyte membrane fuel cells

Haolin Tang,Zhaohui Wan,Mu Pan,San Ping Jiang

DOI: https://doi.org/10.1016/j.elecom.2007.05.024

IF: 5.443

2007-01-01

Electrochemistry Communications

Abstract:In this paper, a novel Nafion/SiO2 nanocomposite membrane based on the self-assembled Nafion–SiO2 nanoparticles was developed. The average particle size of Nafion–SiO2 nanoparticles prepared by self-assembly process was 2.8±0.5nm. The self-assembled Nafion–SiO2 nanoparticles significantly enhance the durability of the Nafion/silica nanocomposite membrane as compared to that of conventional Nafion/silica composite and Nafion 212 membranes under wet/dry cyclic tests at 90°C. With an addition of 5wt% self-assembled Nafion–SiO2 nanoparticles, the Nafion/SiO2 nanocomposite membrane shows a significantly improved performance stability at cell/humidifying temperatures of 100°C/60°C under a current density of 600mA/cm2, and the degradation rate is 0.12mV/min, almost 20 times lower than 2.33mV/min measured on the pristine Nafion 212 membrane under the same conditions. The present results demonstrate the promises of the self-assembled Nafion/SiO2 nanocomposite membrane for elevated-high temperature PEM fuel cells applications.