Abstract:Extraordinary low-temperature vapor-phase synthesis of SnS thin films from single molecular precursors is attractive over conventional high-temperature solid-state methods. Molecular-level processing of functional materials is accompanied by several intrinsic advantages such as precise control over stoichiometry, phase selective synthesis, and uniform substrate coverage. We report here on the synthesis of a new heteroleptic molecular precursor containing (i) a thiolate ligand forming a direct Sn-S bond, and (ii) a chelating O^N^N-donor ligand introducing a “launch vehicle”-effect into the synthesized compound, thus remarkably increasing its volatility. The newly synthesized tin compound [Sn(SBut)(tfb-dmeda)] 1 was characterized by single-crystal X-ray diffraction analysis that verified the desired Sn:S ratio in the molecule, which was demonstrated in the direct conversion of the molecular complex into SnS thin films. The multi-nuclei (1H, 13C, 19F, and 119Sn) and variable-temperature 1D and 2D NMR studies indicate retention of the overall solid-state structure of 1 in the solution and suggest the presence of a dynamic conformational equilibrium. The fragmentation behavior of 1 was analyzed by mass spectrometry and compared with those of homoleptic tin tertiary butyl thiolates [Sn(SBut)2] and [Sn(SBut)4]. The precursor 1 was then used to deposit SnS thin films on different substrates (FTO, Mo-coated soda-lime glass) by CVD and film growth rates at different temperatures (300–450 °C) and times (15–60 min), film thickness, crystalline quality, and surface morphology were investigated.

Fabrication of layered nanocrystallites SnS and β-SnS2 via a mild solution route

Two-dimensional SnS nanosheets fabricated by a novel hydrothermal method

Synthesis of SnS2 nanocrystals via a solvothermal process

Solvent–thermal preparation of nanocrystalline tin chalcogenide

Preparation of ternary I-IV-VI nanocrystallines via a mild solution route

Solution-phase synthesis of monodispersed SnTe nanocrystallites at room temperature

Single-Crystalline Sns2 Nano-Belts Fabricated by A Novel Hydrothermal Method

Synthesis, Characterization, and Properties of Nanocrystalline Cu2sns3

Novel polyol route to nanoscale tin sulfides flaky crystallines

Hydrothermal synthesis, characterization and properties of SnS nanoflowers

Hydrothermal synthesis and characterization of novel aloe-like SnS 2 nanostructures

Solvothermal Synthesis to Cu2snse4 Nanocrystals at Low Temperature

Solvothermal Route to Tin Monoselenide Bulk Single Crystal with Different Morphologies

Solvothermal Synthesis of Cu2ZnSnS4 Nanocrystals by Using Metal Oxides

Preparation and Morphology Control of Rod-like Nanocrystalline Tin Sulfides via a Simple Ethanol Thermal Route

Vapor Phase Synthesis of SnS Facilitated by Ligand-Driven “Launch Vehicle” Effect in Tin Precursors

A convenient, low temperature route to nanocrystalline SnSe

Hydrothermal Synthesis and Characterization of Sns2 Nanocrystals

A hexane solution deposition of SnS2 films from tetrabutyltin via a solvothermal route at moderate temperature

Synthesis of Morphologically Controlled Tin Sulfide Nanostructures

A direct solvothermal route to nanocrystalline selenides at low temperature