Abstract:A simple ultrasonic method was developed to synthesize rod-like SnS nanocrystals, using tin chloride and thioacetamide as starting materials, ethanolamine and water as solvents. The as-obtained nanostructures were characterized by X-ray diffraction (XRD) study, energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and Ultraviolet-visible spectrophotometry (UV). From the XRD pattern, the reflection peaks of the as-obtained samples can be indexed to the orthorhombic structure with lattice constants a = 3.99, b = 4.34, c = 11.20 angstrom, which are very consistent with the values in the standard card of SnS phase (JCPDS No. 39-0354). No characteristic peak was observed for other impurities such as SnO2 and SnS2, implying the formation of single-phase tin monosulfide. The quantification calculation shows the ratio of Sn/S to be 51.30/48.70 via the EDS analysis. These data clearly indicate that the as-prepared rod-like nanostructures are exactly SnS. TEM results show that, the SnS nanorods have length about 100nm and width less than 30nm. The direct and indirect band gaps of the SnS nanorods are determined to be 1.53 eV and 1.34 eV, respectively. The band gaps of the as-obtained SnS nanorods showed blue shifts due to the quantum size effects. The ultrasonic condition is believed to be critical for the formation of SnS with pure phase. For it provides the energy to form rod-like nanostructures and helps preventing the hydrolysis of Sn2+ to form tin oxides and hydrates. Also, it prevents oxidation of the final products.

Preparation and characterization of SnS nanocrystals by a triethanolamine-assisted diethylene glycol solution synthesis

Two-dimensional SnS nanosheets fabricated by a novel hydrothermal method

Green Synthesis by Diethylene Glycol Based Solution Process and Characterization of SnS Nanoparticles

Hydrothermal synthesis and characterization of novel aloe-like SnS 2 nanostructures

Hydrothermal synthesis, characterization and properties of SnS nanoflowers

Studies of synthesis and optical properties of ZnS nanocrystals

Single-Crystalline Sns2 Nano-Belts Fabricated by A Novel Hydrothermal Method

Hydrothermal Synthesis and Characterization of Sns2 Nanocrystals

Colloidal synthesis of metastable zinc-blende IV-VI SnS nanocrystals with tunable sizes.

Sub-2 Nm SnO2 Nanocrystals: A Reduction/oxidation Chemical Reaction Synthesis and Optical Properties

Synthesis of High-Quality and Self-assembled Cu2ZnSnS4 Nanocrystals

Synthesis of SnS2 nanocrystals via a solvothermal process

Ultrasonically Assisted Synthesis of Tin Sulfide Nanorods at Room Temperature

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

Noninjection Synthesis and Characterization of Cu2ZnSnSe4 Nanocrystals in Triethanolamine Reaction Media

Solution-phase synthesis of monodispersed SnTe nanocrystallites at room temperature

Morphology evolution of SnS nanocrystals: from 3D urchin-like architectures to 1D nanostructures

Preparation and characterization of ZnS nanostructures

Synthesis and Characterization of SnS Nanoflakes

Organic solution method for crystal growth of tin chalcogenides with special morphologies

Synthesis, Characterization, and Properties of Nanocrystalline Cu2sns3