Abstract:A series of LiNi0.5Co0.5−xTixO2 (0⩽x⩽0.5) are prepared by a tartaric acid-assisted sol–gel technique. The phase formation process is observed by TG–DTA. It is found that the target product appears at a temperature higher than 400°C and completes to phase formation at 700°C. The crystal structure and morphology are characterized by XRD, SEM and Raman spectroscopy. XRD patterns show that the as-prepared sample transforms from hexagonal structure into cubic structure with the increase of Ti content in LiNi0.5Co0.5−xTixO2. Raman spectra also demonstrate the successive substitution of Ti for Co in the structure with band blue-shift phenomenon. SEM images confirm that the as-prepared sample exhibits narrow and regular particles with the size between 0.5 and 1.5μm. The apparent particle size of sample starts to decrease with x⩽0.1, and the gradually increases by introducing Ti dopant with higher content (x⩾0.15). The electrochemical behavior of the sample displays different characteristics after Ti substitution. It is found that the initial working potential increases with the increase of Ti doping content. As a result, the initial lithium storage capacity for trace Ti-doped sample is higher than that delivered by the pristine one. The decrease of reversible capacity for high degree Ti-doped sample is ascribed to the electrochemical inactivity of the cubic compound in the sample. Therefore, trace Ti doping is beneficial to achieve promising cathode material for lithium-ion batteries.

Synthesis by Sol–gel Process and Characterization of LiCoO2 Cathode Materials

Cathode Materials of Li_xCo_(0.8)Ni_(0.2)O_2 for Lithium-ion Battery

Progress in Research of Positive Materials of Lithium Ion Secondary Batteries and Hydrothermal Synthesis of LiCoO2

Progress in Research on Synthesis of LiNixCo1-xOa Cathode Materials via Sol-gel Methods

Synthesis and performance of S-Co co-doped LiMn2O4

Synthesis, Characterization and Electrochemical Performance of Li[Li0.2Mn0.54Ni0.13Co0.13]O2cathode Materials for Lithium-Ion Batteries

Synthesis and Characterization of Ultrafine LiCoO2 Powders by a Spray-Drying Method

Chemical synthesis and steady state characterization of a nanocrystalline lithium cobalt oxide

Sol-gel synthesis of nano Li1.2Mn0·54Ni0·13Co0·13O2 cathode materials using DL-lactic acid as chelating agent

Nanostructure and Its Effect on Electrochemical Properties of Polyanionic Li2CoSiO4 for Lithium Ion Batteries

From Metal to Cathode Material: in situ Formation of LiCoO2 with Enhanced Cycling Performance and Suppressed Phase Transition

Synthesis of spherical LiCoO2 by emulsion method and the structure, performance research

Tartaric Acid-Assisted Sol–gel Synthesis of LiNi0.5Co0.5−Ti O2 (0 ⩽x⩽ 0.5) As Cathode Materials for Lithium-Ion Batteries

Nanostructure and its effect on electrochemical properties of polyanionic Li 2 CoSiO 4 for lithium ion batteries

Enhanced Cathode Performance: The Heterostructure Construction of LiCoO 2 @Co 3 O 4 @Li 6.4 La 3 Zr 1.4 Ta 0.6 O 12

Synthesis of lithium cobalt oxide of stoichiometric composition by the combined sol-gel method with solid state finishing without using long high-temperature treatment

Study on LiNi_(1-y) Co_yO_2 As Cathode Material for Lithium Ion Batteries

Recent Development in Lithium Ion Battery Cathode Material LiCoO2

Synthesis and Characterization of LiNi0.8Co0.2O2 As Cathode Material for Lithium-Ion Batteries by a Spray-Drying Method

Highly active cathode material LiCoO_2 for lithium ion battery through β-Co(OH)_2 as precursors

Synthesis and characterization of Li(Li0.23Mn 0.47Fe0.2Ni0.1)O2 cathode material for Li-ion batteries