Effect of Composition on the Structural and Electrochemical Properties of (1-X-y)li[li1/3mn2/3]o-2-xlifeo(2)-ylinio(2) Solid Solution Cathode Materials
Jiangang Li,Lei Wang,Yingzhuo Wang,Jianjun Li,Li Wang,Xiangming He
DOI: https://doi.org/10.1016/s1452-3981(23)05034-4
IF: 1.541
2015-01-01
International Journal of Electrochemical Science
Abstract:In view of cost and safety, some Fe-Mn based cathode materials such as LiFeO2-Li2MnO3 solid solution [1], Li(Li0.15Ni0.21Fe0.21Mn0.45)O2 [2] and Li1.2(Mn0.32Ni0.32Fe0.16)O2 [3] etc., were investigated in recent years. Our research group also developed a new cobalt free LiFeO2-Li2MnO3 based solid solution with a composition of Li(Li0.23Mn0.47Fe0.2Ni0.1)O2 to obtain high capacity of 277.4 mAh/g and better cycling stability [4]. In order to further optimize the solid solution composition to obtain the best electrochemical performance, the effects of solid solution composition on Li storage properties should be investigated thoroughly. In this paper, a series of materials with the composition of (1-x-y)Li[Li1/3Mn2/3]O2-xLiFeO2-yLiNiO2(x+y£0.5)were prepared by sol-gel method, and the effect of annealing condition on the structural and electrochemical properties of as-prepared materials were investigated. The results reveal that all of materials prepared at 600 oC ~800 oC show pure layered a-NaFeO2 phase. However, the electrochemical performance varies with the solid solution composition. As shown in Fig.1, as-prepared materials with x+y=0.3~0.4 exhibit better cycling performance, indicating that suitable amounts of composited LiFeO2 and LiNiO2 in the solid solution is benefit for reducing the transformation of layered Li[Li1/3Mn2/3]O2 to spinel phase, and suitable amounts of composited Li[Li1/3Mn2/3]O2 can also restrain cubic LiFeO2 formation. Obvious cooperative effects are observed. In addition, as-prepared samples with high capacity of >210 mAh/g also distribute in this composition range, as shown in shadow area of Fig.1. However, high capacity of above 240 mAh/g can only be obtained while the material with composition of x/y<0.6 and x/y>2 in the shadow range. Further detailed discussion will be presented in the meeting. References [1] M. Tabuchi, Y. Nabeshima, T. Takeuchi, K. Tatsumi, J. Imaizumi, Y. Nitta, J. Power Sources 195 (2010) 834. [2] X. Zheng, L. Cao, W. Zhu, X. Qiu, Acta Chimica Sinica,65 (2007) 571. [3] K. Karthikeyan, S. Amaresh, G.W. Lee, V. Aravindana, H. Kim, K.S. Kang, W.S. Kim, Y.S. Lee, Electrochim. Acta 68 (2012) 246. [4] Jiangang Li, Li Wang, Lei Wang,et al., J. Power Sources 244 (2013) 652. Fig.1 The investigated (1-x-y)Li[Li1/3Mn2/3]O2-xLiFeO2-yLiNiO2 solid solution cathode materials