Tartaric Acid-Assisted Sol–gel Synthesis of LiNi0.5Co0.5−Ti O2 (0 ⩽x⩽ 0.5) As Cathode Materials for Lithium-Ion Batteries

Jie Shu,Miao Shui,Dan Xu,Dongjie Wang,Yuanlong Ren,Jinhan Yao,Rui Ma,Tingfeng Yi,Lifei Li,Shan Gao,Weidong Zheng,Lu Ho,Jinjin Xu,Zhihui Zhu,Min Li

DOI: https://doi.org/10.1016/j.jelechem.2011.10.002

IF: 4.598

2011-01-01

Journal of Electroanalytical Chemistry

Abstract:A series of LiNi0.5Co0.5−xTixO2 (0⩽x⩽0.5) are prepared by a tartaric acid-assisted sol–gel technique. The phase formation process is observed by TG–DTA. It is found that the target product appears at a temperature higher than 400°C and completes to phase formation at 700°C. The crystal structure and morphology are characterized by XRD, SEM and Raman spectroscopy. XRD patterns show that the as-prepared sample transforms from hexagonal structure into cubic structure with the increase of Ti content in LiNi0.5Co0.5−xTixO2. Raman spectra also demonstrate the successive substitution of Ti for Co in the structure with band blue-shift phenomenon. SEM images confirm that the as-prepared sample exhibits narrow and regular particles with the size between 0.5 and 1.5μm. The apparent particle size of sample starts to decrease with x⩽0.1, and the gradually increases by introducing Ti dopant with higher content (x⩾0.15). The electrochemical behavior of the sample displays different characteristics after Ti substitution. It is found that the initial working potential increases with the increase of Ti doping content. As a result, the initial lithium storage capacity for trace Ti-doped sample is higher than that delivered by the pristine one. The decrease of reversible capacity for high degree Ti-doped sample is ascribed to the electrochemical inactivity of the cubic compound in the sample. Therefore, trace Ti doping is beneficial to achieve promising cathode material for lithium-ion batteries.