Molecular Engineering of Liquid Crystal Polymers by Living Polymerization. VIII. Influence of Molecular Weight on the Phase Behavior of Poly {Ω-[(4-cyano-4′-biphenyl)-oxy]alkyl Vinyl Ether}s with Ethyl, Propyl, and Butyl Alkyl Groups
Virgil Percec,Myongsoo Lee
DOI: https://doi.org/10.1080/00222339108052116
1991-01-01
Abstract:The synthesis and living cationic polymerization of 2-[4-cyano-4′-biphenyl)oxy]ethyl vinyl ether (6–2), 3-[4-cyano-4′-biphenyl)oxy]-propyl vinyl ether (6-3), and 4-[4-cyano-4′-biphenyl)oxy]butyl vinyl ether (6-4) are described. The mesomorphic behaviors of poly(6–2), poly(6-3), and poly(6-4) with different degrees of polymerization and narrow molecular weight distributions were compared to those of 6–2, 6–3, and 6–4 and of 2-[(4-cyano-4′-biphenyl)oxy]ethyl ethyl ether (8–2), 3-[(4-cyano-4′-biphenyl)oxy]propyl ethyl ether (8–3), and 4-[4-cyano-4′-biphenyl)oxy]butyl ethyl ether (8–4) which are model compounds of the monomeric structural units of poly(6–2), poly(6–3), and poly(6–4). In the first heating scan, all three polymers exhibit an x (unidentified) mesophase which overlaps the glass transition temperature, and an enantiotropic nematic mesophase. In the second and subsequent heating and cooling scans, poly(6–3) and poly(6–4) display only the enantiotropic nematic mesophase. Both in the first and subsequent scans, only poly(6–2) with degrees of polymerization lower than 4 exhibits an enantiotropic nematic mesophase.