Molecular Engineering of Liquid-Crystalline Polymers by Living Polymerization. Part 13.—synthesis and Living Cationic Polymerization of (S)-(–)-2-methylbutyl 4′-(Ω-vinyloxy)alkoxybiphenyl-4-carboxylate with Undecanyl and Hexyl Alkyl Groups

V PERCEC,QA ZHENG,M LEE

DOI: https://doi.org/10.1039/jm9910100611

1991-01-01

Journal of Materials Chemistry

Abstract:The synthesis and living cationic polymerization of (S)-(-)-2-methylbutyl 4'-(11-vinyloxy)undecyloxybiphenyl-4-carboxylate (13-11) and (S)-(-)-2-methylbutyl 4'-(6-vinyloxy)hexyloxybiphenyl-4-carboxylate (13-6) are described. Polymers with degrees of polymerization from 4 to 26 and polydispersities less-than-or-equal-to 1.10 were synthesized and characterized by differential scanning calorimetry (DSC) and thermal optical polarized microscopy. When determined from first heating and cooling DSC scans, poly(13-11) exhibits monotropic s(A), s(c)* and s(x) (unidentified) mesophases over the entire range of molecular weights. When determined from second and subsequent heating and first and subsequent cooling scans, poly(13-11) with degrees of polymerization less-than-or-equal-to 10 exhibit enantiotropic s(A), s(c)* and s(x) mesophases, and crystallization on the heating scan, while those with higher degrees of polymerization exhibit enantiotropic s(A), s(c)* and s(x) mesophases only. Regardless of the thermal history of the sample, poly(13-6) exhibits an enantiotropic s(A) phase, and the polymers with degrees of polymerization > 12 exhibit an enantiotropic s(x) mesophase as well.