Abstract:Atom transfer radical polymerization(ATRP) was applied to prepare an amphiphilic azobenzene-containing ABA triblock copolymer PMAA-b-PMAZOCNb-PMAA.In the presence of(4,4′-di(n-nonyl)-2,2′-)bipyridine(bpy9) and CuBr(as the catalyst),the dibromo-initiator butylene di(2-bromoisobutyrate) was reacted with the azobenzene-containing monomer,6-[4-(4′-cyanophenylazo)phenoxy]hexyl methacrylate(MAZOCN),which resulted in the macro-initiator.The absolute molecular weight of the macro-initiator was obtained by GPC-SLS(gel permeation chromatography-static light scattering) method.The dn/dc of the macro-initiator was predetermined as 0.257 mL/g by the refractometer.Then CuCl was used as the catalyst,and the macro-initiator further reacted with the tert-butyl methacrylate to obtain the triblock copolymer PtBMA-b-PMAZOCN-PtBMA as a precursor.From()~1H-NMR,the polymerization of tBMA monomers initiated by the macro-initiator was proved by the presence of a rather strong resonance at δ=1.43 which is corresponding to the tert-butyl group.A single Gaussian peak in the GPC curves further proved the narrow polydispersity of the resultant precursor triblock copolymer.The absolute molecular weight of the triblock copolymer was obtained by combination of the segement molar ratio determined from the characteristic ~1H-NMR peaks and the absolute molecular weight of the macroinitiator.In the final step,the tert-butyl groups were removed by the selective hydrolysis reaction with trifluoroacetic acid at room temperature.~1H-NMR analyses proved that most of the tert-butyl groups were hydrolyzed(conversion 95%),while the ester groups in the azo blocks were retained.These monomers and polymers were then studied with PLM(polarized light microscopy) and DSC(differential scanning calorimetry).The monomer,macro-initiator and the precursor triblock copolymer are all own smectic phase in the liquid crystalline region,while no characteristic liquid crystalline texture could be observed for the amphiphilic triblock copolymers.It is possibly because that,the presence of H-bonds between carboxyl groups hindered the development of the liquid crystalline phase.The amphiphilic ABA triblock copolymer possessed hydrophilic blocks in the outer part and the hydrophobic block in the central part.The vesicular aggregates of the polymer were obtained by gradually adding water,which is the good solvent of the hydrophilic block and the poor solvent of the azobenzene-containing liquid crystalline block,into the stirring THF solution of the amphiphilic copolymer.When the water content was more than 50% volume ratio,an excessive amount of water was added to freeze the assembly of the copolymer.THF was removed from the mixed solvent by dialyzed against ultrapure water for days.The TEM(transmission electron microscopy) observation showed that the amphiphilic block copolymer self-assembled into vesicular aggregates with average diameters from 300 to 500 nm.By using a high-pressure mercury lamp as the light source,the vesicular aggregates transform to the colloidal spheres when irradiated with the ultraviolet light in the solid state.

SYNTHESIS AND CHARACTERIZATION OF A LIQUID CRYSTALLINE TRIBLOCK COPOLYMER CONTAINING ETHOXYCARBONYLAZOBENZENE UNITS

Preparation of Triblock Copolymers with High &ITCis&IT-1,4-polybutadiene as Soft Segments

Azobenzene-Containing Liquid Crystal Triblock Copolymers: Synthesis, Characterization, and Self-Assembly Behavior

ABA-type amphiphilic triblock copolymers containing p-ethoxy azobenzene via atom transfer radical polymerization: synthesis, characterization, and properties

Synthesis, Characterization and Self-Assembly of an Azobenzene-Containing Amphiphilic Aba Triblock Copolymer

Novel Amphiphilic Diblock and Triblock Liquid-Crystalline Copolymers with Well-Defined Structures Prepared by Atom Transfer Radical Polymerization

SYNTHESIS AND CHARACTERIZATION OF THERMOTROPIC POLYAMIDE LIQUID CRYSTALLINE BLOCK COPOLYMERS

Diblock copolymers composed of a liquid crystalline azo block and a poly(dimethylsiloxane) block: synthesis, morphology and photoresponsive properties

Aba Type Triblock Copolymer Based on Mesogen-Jacketed Liquid Crystalline Polymer: Design, Synthesis, and Potential As Thermoplastic Elastomer

Interplay of Microphase Separation, Crystallization and Liquid Crystalline Ordering in Crystalline/liquid Crystalline Block Copolymers

Synthesis and Characterization of Liquid Crystalline Multi-Block Copolymers, Poly[1,6-Bis(4-Oxybenzoyl-Oxy)Hexane Terephthalate]-B-Bisphenol A Polycarbonate

Effect of the Amorphous Segment on the Nonisothermal Crystallization and Morphology of Oxyethylene–oxybutylene Block Copolymers

Synthesis and Characterization of H-type Amphiphilic Liquid Crystalline Block Copolymers by ATRP

Synthesis and Characterization of Poly(dimethylamino Ethyl Methacrylate)–poly(ethylene Oxide)–poly(dimethylamino Ethyl Methacrylate) Triblock Copolymers

Observation of Double Gyroid and Hexagonally Perforated Lamellar Phases in ABCBA Pentablock Terpolymers

Synthesis and dielectric properties of novel liquid crystalline triblock copolymers with cyanobiphenyl moieties and poly(n‐butyl acrylate) segments

ABA Type Liquid Crystalline Triblock Copolymers by Combination of Living Cationic Polymerizaition and ATRP: Synthesis and Self-Assembly.

Solution Crystallization Behavior Of Crystalline-Crystalline Dibloek Copolymers Of Poly(Ethylene Oxide)-Block-Poly(Epsilon-Caprolactone)

Effect of the terminal substituent of azobenzene on the properties of ABA triblock copolymers via atom transfer radical polymerization

Synthesis and Characterization of Novel Rod–coil Diblock Copolymers of Poly(methyl Methacrylate) and Liquid Crystalline Segments of Poly(2,5‐bis[(4‐methoxyphenyl)oxycarbonyl] Styrene)

Syntheses and Characterizations of Poly[2‐(dimethylamino)ethyl Methacrylate]–poly(propylene Oxide)–poly[2‐(dimethylamino)ethyl Methacrylate] ABA Triblock Copolymers