A Novel Orange Phosphor of Eu2+-activated Calcium Chlorosilicate for White Light-Emitting Diodes

Weijia Ding,Jing Wang,Mei Zhang,Qiuhong Zhang,Qiang Su

DOI: https://doi.org/10.1016/j.jssc.2006.07.007

IF: 3.3

2006-01-01

Journal of Solid State Chemistry

Abstract:Novel orange phosphor of Eu2+-activated calcium chlorosilicate was synthesized at 1273K by conventional solid-state reactions under reductive atmosphere and investigated by means of photoluminescence excitation, diffuse reflectance and emission spectroscopies. These results show that this phosphor can be efficiently excited by the incident light of 300–450nm, well matched with the emission band of 395nm-emitting InGaN chip, and emits an intense orange light peaking at 585nm. By combining this phosphor with a 395nm-emitting InGaN chip, an intense orange light-emitting diode (LED) was fabricated. Under 20mA forward-bias current, its CIE chromaticity coordinates are (0.486, 0.446). The dependence of as-fabricated orange LED on forward-bias current indicates that it shows excellent chromaticity stability and luminance saturation. These results show that this Eu2+-activated calcium chlorosilicate is a promising orange-emitting phosphor for near-ultraviolet (UV) InGaN-based white LED.