Development of a novel Eu2+ activated oxonitridosilicate cyan phosphor for enhancing the color quality of violet-chip-based white LED

Langping Dong,Jinqing Gao,Yijia Guo,Jingshan Hou,Baiqi Shao,Yongzheng Fang

DOI: https://doi.org/10.1039/d3dt04188c

IF: 4

2024-01-25

Dalton Transactions

Abstract:Cyan phosphor is urgently needed to fill the cyan gap and improve the spectral continuity of white light-emitting diodes (LEDs) to cater to the high criteria for high-quality lighting. Here a series of new Eu2+-activated La3Si6.5Al1.5N9.5O5.5 (LSANO) cyan phosphors were prepared, and their luminescent properties and color center were analyzed through fluorescence spectra measurements from 7 K to 475 K. At 300 K, the photoluminescence excitation (PLE) spectrum monitoring at 483 nm presents a broadband of 200 – 460 nm with a peak at 398 nm, matching well with the commercial violet LED chips. When excited by 398 nm violet light, the photoluminescence emission (PL) spectrum of LSANO:0.01Eu2+ exhibits a cyan emission band at about 483 nm. At 7 K, the emission spectrum is a clearly asymmetric emission band and the emission peak wavelength changes from 483 nm (300 K) to 500 nm (7 K), indicating that there are two possible color centers in LSANO:Eu2+ phosphor. Moreover, the maximum emission value can be adjusted from 480 to 499 nm by adjusting the doping content of Eu2+. Finally, a violet-chip-based white LED with optimized color quality of Ra = 91.4, Rf = 90.1, and Rg = 93.6 was fabricated by adding the prepared cyan phosphor, verifying the potential application of the prepared cyan phosphor LSANO:Eu2+ in high-quality white LEDs.

chemistry, inorganic & nuclear