Abstract:A new type of waterborne polyurethane acrylate was synthesized for use as a UV curing coating. The N,N-dihydroxy methyl ethyl-3-Methyl aminopropanoate monomer was first prepared via adding reactions of methyl acrylate and diethanol amine with methyl alcohol as the solvent. Then, the hyperbranched prepolymer was obtained by addition of trimethylolpropane with toluenesulfonic acid as catalyst and N,N-dimethyl formamide as solvent. The resulting hyperbranched and organosilicone modified waterborne polyurethane acrylates was synthesized through the mixed reaction of prepolymer and Hydroxy silicone oil, polyethylene glycol-1000, toluene diisocynate, dimethylolpropionic acid, 1,2-propylene glycol, hydroxyethyl acrylate, and triethylamine with dibutyltin dilaurate as the catalyst. The molecular structures were characterized by FT-IR and 1H NMR spectroscopy and GPC analysis and the thermal stability was studied by using TGA. Moreover, the influence of contemodnt of hydroxyl silicone oil, dimethylolpropionic acid, polyethylene glycol-1000, and prepolymer to various of properties such as glossiness, hardness, adhesive force, abrasion resistance, water absorption, elongation at break and tensile strength of films were analyzed. The temperature and catalyst dosage impact on percent conversion of isocyanate group (–NCO) were also studied. It was proven that the best dosage of hydroxyl silicone oil and dimethylolpropionic acid were 4.6%, the dosage of polyethylene glycol-1000 was 50%, and the amount of hyperbranched prepolymer was 0.5%, which could make the film achieve the optimum properties. The percent conversion of isocyanate group (–NCO) was maximum when reacting two hours at 80 °C with 0.2% catalyst.

Study on Synthesis of Cationic Waterborn Acrylate Resin and Characterization

Synthesis of Water-soluble Acrylic-Styrene Copolymer

STUDY OF THE SYNTHESIS OF WATER-BORNE ACRYLIC COPOLYMER FOR MODIFICATION OF BOPET FILM

Preparation of waterborne automotive coatings and investigation of viscosity

Preparation and Characterization of Polyol - Anionic Waterborne Polyurethane Adhesive

Study on the Cationic AM/DMC Copolymer

Preparation of Dendritic Hyperbranched Polyester Modified Acrylic Resin and Study on Properties of Its Waterborne Coating Films

Synthesis and Characterization of Self-cross Linking Hybrid Silicone-acrylate Emulsion at Ambient Temperature

Study on Application of Alcohol-Soluble Polyacrylate by Semi-Bulk Polymerization in Fast-Dried Coating

Study on the UV-curable waterborne alicyclic epoxy acrylates

Study On The Synthesis And Properties Of Water Soluble Superplasticizer With Side Branch Poly(Ethylene Glycol) Methyl Ether

Preparation of low‐temperature self‐crosslinking acrylic resin and its performance research

Synthesis of cationic polyacrylamide via inverse emulsion polymerization method for the application in water treatment

Study on hydroxyl acrylic resin containing cyclic anhydride

Characterization and solution properties of acrylamide/(2-methacryloyloxyethyl) trimethylammonium chloride/dimethyldiallylammonium chloride terpolymer

Preparation, Characterization and Solution Properties of Poly(AM/DMC/C(11)AM)

Preparation and Properties of Polyester Modified Waterborne High Hydroxyl Content and High Solid Content Polyacrylate Emulsion

Synthesis and Characterization of Hyperbranched and Organosilicone Modified Waterborne Polyurethane Acrylates Photosensitive Resin

A comprehensive study on the application properties of different soft, hard, and functional monomers to polyacrylate emulsion and water‐based inks

Synthesis, kinetics and characterization of environment friendly waterborne acrylate copolymers

Synthesis and characterization of acrylic rubber